Zamzam Water as Corrosion Inhibitor for Steel Rebar in Rainwater and Simulated Acid Rain
نویسنده
چکیده
Abstract—Corrosion inhibitors are widely used in concrete industry to reduce the corrosion rate of steel rebar which is present in contact with aggressive environments. The present work aims to using Zamzam water from well located within the Masjid al-Haram in Mecca, Saudi Arabia 20 m (66 ft) east of the Kaaba, the holiest place in Islam as corrosion inhibitor for steel in rain water and simulated acid rain. The effect of Zamzam water was investigated by electrochemical impedance spectroscopy (EIS) and Potentiodynamic polarization techniques in Department of Civil Engineering IUT Saint-Nazaire, Nantes University, France. Zamzam water is considered to be one of the most important steel corrosion inhibitor which is frequently used in different industrial applications. Results showed that zamzam water gave a very good inhibition for steel corrosion in rain water and simulated acid rain.
منابع مشابه
INVESTIGATION ON THE MIXTURE OF CALCIUM AND AMMONIUM NITRATES AS STEEL CORROSION INHIBITOR IN SIMULATED CONCRETE PORE SOLUTION
Abstract: Despite having a number of advantages, reinforced concrete can suffer rebar corrosion in high–chloride media, resulting in failure of reinforced concrete structures. In this research the corrosion inhibition capability of the mixture of calcium and ammonium nitrate of steel rebar corrosion was investigated in the simulated concrete pore solution. Cyclic polarization and Electroche...
متن کاملINVESTIGATION INTO SYNERGISTIC EFFECT OF MOLYBDATE AND PHOSPHATE AS AN INHIBITOR FOR MILD STEEL CORROSION PREVENTION IN SIMULATED COOLING WATER
The synergistic behavior of molybdate and phosphate ions in mitigating the corrosion of mild steel in simulated cooling water was evaluated performing potentiodynamic polarization and impedance spectroscopy tests. Phosphate and molybdate showed a synergistic effect on corrosion inhibition of steel in simulated cooling water. The observed reduction in anodic and cathodic current densities could ...
متن کاملBoric Acid Corrosion of Concrete Rebar
Borated water leakage through spent fuel pools (SFPs) at pressurized water reactors is a concern because it could cause corrosion of reinforcement steel in the concrete structure and compromise the integrity of the structure. Because corrosion rate of carbon steel in concrete in the presence of boric acid is lacking in published literature and available data are equivocal on the effect of boric...
متن کاملInhibition Effect of Vernonia amygdalina Extract on the Corrosion of Mild Steel Reinforcement in Concrete in 3.5M NaCl Environment
The inhibition effect of Vernonia amygdalina (bitter leaf) extract on the corrosion behaviour of embedded mild steel rebar in concrete has been investigated by electrochemical potential measurement, pH and gravimetric (weight loss) methods. The results were further analysed using the two-factor ANOVA test. The experiments were performed using bitter leaf extract as a green inhibitor in 3.5% sod...
متن کاملRapid Synthesis and Evaluation of a Cheaper Corrosion Inhibitor for Steel in HCl Solution
A corrosion inhibitor suitable for industrial production and field application was rapidly synthesized from benzene-1,2-diamine, benzaldehyde, methanol, hydrochloric acid, and FeCl3. The mechanism of corrosion and its inhibition was proposed. We investigated the effect of the main reactants on corrosion rate, and optimal synthetic composition (benzene-1,2-diamine 10 g, b...
متن کامل