Structure and corrosion behavior of platinum/ruthenium/nitrogen doped diamondlike carbon thin films
نویسندگان
چکیده
Platinum/ruthenium/nitrogen doped diamondlike carbon PtRuN-DLC thin films were deposited on p-Si 100 substrates with dc magnetron cosputtering by varying the dc power applied to a Pt50Ru50 target to investigate the effect of Pt and Ru incorporation in the films on the bonding structure, adhesion strength, surface morphology, and corrosion behavior of the films by means of X-ray photoelectron spectroscopy, micro-Raman spectroscopy, microscratch test, atomic force microscopy, scanning electron microscopy, and potentiodynamic polarization test. It was found that the incorporation of Pt and Ru in the N-DLC films improved the corrosion resistance of the films in a 0.1M NaCl solution at lower polarization potentials though more sp2 bonds were formed in the films. However, the films with higher Pt and Ru contents degraded earlier than the ones with lower Pt and Ru contents at higher polarization potentials. © 2009 American Institute of Physics. DOI: 10.1063/1.3154022
منابع مشابه
Investigation of corrosion behavior of nitrogen doped and platinum/ruthenium doped diamond-like carbon thin films in Hank's solution
متن کامل
Investigation of structure, adhesion strength, wear performance and corrosion behavior of platinum/ruthenium/nitrogen doped diamond-like carbon thin films with respect to film thickness
In this study, the corrosion performance of platinum/ruthenium/nitrogen doped diamond-like carbon (PtRuN-DLC) thin films deposited on p-Si substrates using a DCmagnetron sputtering deposition system in a 0.1M NaCl solution was investigated using potentiodynamic polarization test in terms of film thickness. Theeffect of thefilmthickness on the chemical composition, bonding structure, surfacemorp...
متن کاملEnhancement of adhesion strength and corrosion resistance of nitrogen or platinum/ruthenium/nitrogen doped diamond-like carbon thin films by platinum/ruthenium underlayer
متن کامل
Influence of carbon sputtering power on structure, corrosion resistance, adhesion strength and wear resistance of platinum/ruthenium/nitrogen doped diamond-like carbon thin films
متن کامل
Nitrogen-Induced Degradation of Corrosion Resistance of Platinum/Ruthenium/Nitrogen-Doped Diamond-like Carbon Thin Films
An influence of nitrogen incorporation on the chemical composition, bonding structure, surface morphology and activity, adhesion strength, and corrosion resistance of platinum/ruthenium/nitrogen-doped diamond-like carbon PtRuN-DLC thin films deposited on conductive p-Si 100 substrates using dc magnetron sputtering deposition was investigated using X-ray photoelectron spectroscopy, micro-Raman s...
متن کامل