Direct synthesis of ultrafine tetragonal BaTiO3 nanoparticles at room temperature
نویسندگان
چکیده
A large quantity of ultrafine tetragonal barium titanate (BaTiO3) nanoparticles is directly synthesized at room temperature. The crystalline form and grain size are checked by both X-ray diffraction and transmission electron microscopy. The results revealed that the perovskite nanoparticles as fine as 7 nm have been synthesized. The phase transition of the as-prepared nanoparticles is investigated by the temperature-dependent Raman spectrum and shows the similar tendency to that of bulk BaTiO3 materials. It is confirmed that the nanoparticles have tetragonal phase at room temperature.
منابع مشابه
Structure Evolution and Dielectric Behavior of Polystyrene-Capped Barium Titanate Nanoparticles
Polystyrene-capped barium titanate (BaTiO3) nanoparticles with sizes of 11 nm and 27 nm were prepared using amphiphilic star-like diblock copolymer templates. The crystal structure evolution of these nanoparticles over a wide temperature range (10-428 K) was investigated by powder X-ray diffraction. The Rietveld refinement indicates that the abrupt structural transitions observed in micron-size...
متن کاملMagnetic hardening in ultrafine FePt nanoparticle assembled films
Ultrafine FePt nanoparticles have been synthesized via a novel chemical solution synthesis route. Without using a reducing agent, the stoichiometric FePt nanoparticles were produced by the decomposition of iron acetylacetonate and platinum acetylacetonate in octyl ether in the presence of oleic acid and oleyl amine as the surfactants. The particle size was found to be around 2 nm with a narrow ...
متن کاملSol-gel synthesis of (Ca-Ba)TiO3 nanoparticles for bone tissue engineering
Piezoelectric materials are the group of smart materials which have been recently developed for biomedical applications, such as bone tissue engineering. These materials could provide electrical signals with no external source power making them effective for bone remodeling. Between various types of materials, BaTiO3 and CaTiO3 are nontoxic piezoelectric ceramics, which recently have been intro...
متن کاملSURFACTANT-ASSISTED SYNTHESIS OF BaTiO3 NANOPARTICLES BY MICRO-EMULSION METHOD
J. L. Gao, Y. Zhi, X. F. Ren, Y. H. Liu, College of Material Science and Engineering, Shenyang Ligong University, Shenyang, Liaoning, China. Barium titanate (B aTiO3) nanoparticles were successfully synthesized by using a surfactant-assisted method. The various processing parameters, namely, th e species of surfactant, reaction temperature and micro-emusion concentration had been varied, and th...
متن کاملEffect of Crystalline Size on the Structure of Copper Doped Zirconia Nanopaticles Synthesized via Sol-Gel
The stabilized zirconia with different Cu contents synthesized via sol- gel method. The samples were prepared by hydrolysis and condensation of orgnomatelic sol. After that the result gels were dried at 80 °C and then calcined at various temperatures. ِ The differential thermal analysis (DTA), X-ray diffraction (XRD), field emission scanning electronic microscopy (FESEM) and transmission el...
متن کامل