The Influence of Deposition Methods of Support Layer on Cordierite Substrate on the Characteristics of a MnO2–NiO–Co3O4/Ce0.2Zr0.8O2/Cordierite Three Way Catalyst
نویسندگان
چکیده
This paper compares different coating methods (in situ solid combustion, hybrid deposition, secondary growth on seed, suspension, double deposition of wet impregnation and suspension) to deposit Ce0.2Zr0.8O₂ mixed oxides on cordierite substrates, for use as a three way catalyst. Among them, the double deposition was proven to be the most efficient one. The coated sample shows a BET (Brunauer-Emmett-Teller) surface area of 25 m²/g, combined with a dense and crack free surface. The catalyst with a layer of MnO₂-NiO-Co₃O₄ mixed oxides on top of the Ce0.2Zr0.8O₂/cordierite substrate prepared by this method exhibits good activity for the treatment of CO, NO and C₃H₆ in exhaust gases (CO conversion of 100% at 250 °C, C₃H₆ conversion of 100% at 400 °C and NO conversion of 40% at 400 °C).
منابع مشابه
Investigation on Mechanism of Cordierite Formation from Nano Silica-Magnesium chloride-Reactive Alumina
Cordierite ceramics are used as refractory materials and kiln furnaces tools due to their very low coefficient of thermal expansion, high corrosion resistance and excellent thermal shock resistance. The aim of the present work was to synthesis of cordierite with raw materials including nano silica, magnesium chloride and reactive alumina. The synthesis procedure is done at solid state. Mechanis...
متن کاملTwo-Stage Chemical Deposition of Oxide Films
Two-stage chemical deposition (TSCD) technique is used to produce ZnO, Mn2O3 and NiO films on soda-lime glass (SL-G) from an aqueous solution of zinc, manganese and nickel complex, respectively. The TSCD method enables the deposition of metal oxide thin films with a thickness which can be controlled during the preparation procedure. The ZnO, Mn2O3 and NiO thin films were polycrystalline films w...
متن کاملEFFECT OF COMPOSITION AND PREPARATION METHOD OF (Pd), Co, Ce, Zr - METAL-OXIDE CATALYSTS ON THEIR ACTIVITY IN THE REDUCTION OF NITROGEN(I), (II) OXIDES WITH CARBON MONOXIDE
Among the studied (Pd), Co-, Ce-, Zr-oxide catalysts including catalysts deposited on structured cordierite support, the catalyst prepared by co-deposition of ceria and cobalt oxide is characterized by higher activity in reaction of reduction of nitrogen(I), (II) oxides (CO + NO, N2O + NO + CO) compared with samples prepared by successive deposition. This may be caused by an increase in both mo...
متن کاملPoisoning Effect of SO2 on Honeycomb Cordierite- Based Mn–Ce/Al2O3Catalysts for NO Reduction with NH3 at Low Temperature
Honeycomb cordierite-based Mn–Ce/Al2O3 catalysts were prepared by the impregnation method and used for low-temperature selective catalytic reduction (SCR) of NOx with NH3, with and without SO2 and/or H2O in a homemade fixed-bed tubular reactor. The catalyst reached nearly 80% NOx conversion at 100 ◦C in the absence of SO2. However, SO2 reduces the catalytic activity (80% to 72%) of the honeycom...
متن کاملNON-DESTRUCTIVE THERMAL DAMAGE CHARACTERIZATION OF CORDIERITE-MULLITE REFRACTORIES
Abstract: Refractory materials containing cordierite (2MgO.2Al2O3.5SiO2) and mullite (3Al2O3.2SiO2) are used as support in furnaces, because of their low thermal expansion properties which confer them a very good ability to thermal shock resistance. Composed of two phases presenting very different CTE (1.5–3×10-6 for cordierite and 4–6×10-6 K-1 for mullite), these materials can develop damag...
متن کامل