Growth of TiN on WC surfaces
نویسندگان
چکیده
منابع مشابه
Wear Behavior of Fiber Laser Textured TiN Coatings in a Heavy Loaded Sliding Regime
In heavy loaded mating components, such as sliders and sliding bearings, guaranteeing the efficiency of lubricant films for long times during severe service conditions is very complicated. In this work, the benefits deriving from the use of fiber laser sources for surface texturing of very thin TiN coatings in severe wear working conditions were demonstrated. Evaluations of the laser textured d...
متن کاملEffect of Carbide Particle Size on the Microstructure, Mechanical properties, and Wear Behavior of HVOF-sprayed WC-17% Co Coatings
This study investigates the effect of carbide particle size on the microstructure, mechanical properties, and abrasive wear resistance of WC-17%Co HVOF-sprayed coatings. The characteristics of WC-1, WC-2, and WC-3 coatings with carbide sizes of 1 µm, 0.9 µm, and 0.5 µm, respectively, were also investigated. WC-1 coating experienced the maximum carbon loss of 42%, while WC-2 and WC-3 coatings un...
متن کاملEvaluation of fracture strength of TiN thin films deposited on WC-Co substrate
To evaluate the fracture strength of TiN thin films deposited on the hard metal substrate WC-Co, and to investigate the influence of the deposition conditions (bias voltage VB) on the fracture strength of TiN thin films, the sphere indentation test was carried out to determine the ring crack initiation strength σf,m in TiN thin films deposited on two kinds of WC-Co substrates differing in hardn...
متن کاملEffect of Surface Roughness Morphology on Bond Strength of Thermal Sprayed WC-10Co-4Cr Ceramic/Metal Coating
In this study, the effect of surface roughness and roughness morphology on the bond strength of WC-Co-Cr coatings has investigated. The three different surfaces morphology are use for this purpose. The first and tow samples sandblasted with alumina and silicon carbide respectively. Other sample no sandblasted before spraying process. The same WC-10Co-4Cr coating deposited on the substrates with...
متن کاملSurface observation for seed-mediated growth attachment of gold nanoparticles on a glassy carbon substrate.
A seed-mediated growth method for surface modification was applied to the attachment of gold nanoparticles (AuNPs) to glassy carbon (GC) surfaces. By simply immersing a GC plate at first into a seed solution containing 4 nm Au nano-seed particles and then into a growth solution containing HAuCl(4), ascorbic acid and cetyltrimethyammonium bromide, AuNPs could be successfully attached to the GC s...
متن کامل