Bactericidal and antimicrobial effects of pure titanium and titanium alloy treated with short-term, low-energy UV irradiation
نویسندگان
چکیده
OBJECTIVES The surface of pure titanium (Ti) shows decreased histocompatibility over time; this phenomenon is known as biological ageing. UV irradiation enables the reversal of biological ageing through photofunctionalisation, a physicochemical alteration of the titanium surface. Ti implants are sterilised by UV irradiation in dental surgery. However, orthopaedic biomaterials are usually composed of the alloy Ti6Al4V, for which the antibacterial effects of UV irradiation are unconfirmed. Here we evaluated the bactericidal and antimicrobial effects of treating Ti and Ti6Al4V with UV irradiation of a lower and briefer dose than previously reported, for applications in implant surgery. MATERIALS AND METHODS Ti and Ti6Al4V disks were prepared. To evaluate the bactericidal effect of UV irradiation, Staphylococcus aureus 834 suspension was seeded onto the disks, which were then exposed to UV light for 15 minutes at a dose of 9 J/cm2. To evaluate the antimicrobial activity of UV irradiation, bacterial suspensions were seeded onto the disks 0, 0.5, one, six, 24 and 48 hours, and three and seven days after UV irradiation as described above. In both experiments, the bacteria were then harvested, cultured, and the number of colonies were counted. RESULTS No colonies were observed when UV irradiation was performed after the bacteria were added to the disks. When the bacteria were seeded after UV irradiation, the amount of surviving bacteria on the Ti and Ti6Al4V disks decreased at 0 hours and then gradually increased. However, the antimicrobial activity was maintained for seven days after UV irradiation. CONCLUSION Antimicrobial activity was induced for seven days after UV irradiation on both types of disk. Irradiated Ti6Al4V and Ti had similar antimicrobial properties.Cite this article: T. Itabashi, K. Narita, A. Ono, K. Wada, T. Tanaka, G. Kumagai, R. Yamauchi, A. Nakane, Y. Ishibashi. Bactericidal and antimicrobial effects of pure titanium and titanium alloy treated with short-term, low-energy UV irradiation. Bone Joint Res 2017;6:108-112. DOI: 10.1302/2046-3758.62.2000619.
منابع مشابه
Effect of Photodynamic Therapy Using Toluidine Blue on Eikenella corrodens and Aggregatibacter actinomycetemcomitans Biofilms Adhered to Titanium Discs: An In Vitro Study
Background and aim: Antimicrobial photodynamic therapy (aPDT) has been suggested as a novel technique for decontamination of exposed implant surfaces. We aimed to evaluate the effect of aPDT on sandblasted, large-grit, acid-etched (SLA) titanium discs contaminated with Eikenella corrodens (Ec) and Aggregatibacter actinomycetemcomitans (Aa). Materials and methods: In this in-vitro study, twenty...
متن کاملAg-doped TiO2 Nanocomposite Prepared by Sol Gel Method: Photocatalytic Bactericidal Under Visible Light and Characterization
In this reaserch, photocatalyst titanium dioxide was doped with silver and modified by polyethylene glycol by sol gel method and the samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The purpose of the present study was to evaluate the photocatalytic bactericidal effects of prepared nanocomposite on human p...
متن کاملUV/H2O2/TiO2/Zeolite Hybrid System for Treatment of Molasses Wastewater
Wastewater from molasses processing contains a large amount of coloured substances that give a recalcitrant dark brown colour and high organic load to the effluent. Photocatalytic decolourization of molasses wastewater was performed using titanium dioxide catalyst coated on the surface of South African natural zeolite using the solid-solid dispersion method. Addition of hydrogen peroxide as...
متن کاملFriction stir welding of dissimilar joint of aluminum alloy 5083 and commercially pure titanium
In this study, commercially pure titanium and aluminum alloy 5083 in connection rotational speed of 1120 rpm and a feed rate of 50 mm per minute for butt welding by friction stir welding has been successfully completed. Micro-structure, hardness and tensile test was conducted on the connection. Welding area is a composite of aluminum and titanium particles that the particles plays an important ...
متن کاملVisible-light-induced bactericidal activity of a nitrogen-doped titanium photocatalyst against human pathogens.
The antibacterial activity of photocatalytic titanium dioxide (TiO(2)) substrates is induced primarily by UV light irradiation. Recently, nitrogen- and carbon-doped TiO(2) substrates were shown to exhibit photocatalytic activities under visible-light illumination. Their antibacterial activity, however, remains to be quantified. In this study, we demonstrated that nitrogen-doped TiO(2) substrate...
متن کامل