Preparation of Aligned Ultra-long and Diameter-controlled Silicon Oxide Nanotubes by Plasma Enhanced Chemical Vapor Deposition Using Electrospun PVP Nanofiber Template
نویسندگان
چکیده
Well-aligned and suspended polyvinyl pyrrolidone (PVP) nanofibers with 8 mm in length were obtained by electrospinning. Using the aligned suspended PVP nanofibers array as template, aligned ultra-long silicon oxide (SiOx) nanotubes with very high aspect ratios have been prepared by plasma-enhanced chemical vapor deposition (PECVD) process. The inner diameter (20-200 nm) and wall thickness (12-90 nm) of tubes were controlled, respectively, by baking the electrospun nanofibers and by coating time without sacrificing the orientation degree and the length of arrays. The micro-PL spectrum of SiOx nanotubes shows a strong blue-green emission with a peak at about 514 nm accompanied by two shoulders around 415 and 624 nm. The blue-green emission is caused by the defects in the nanotubes.
منابع مشابه
Excimer laser nanostructuring of nickel thin films for the catalytic growth of carbon nanotubes
Pulse laser ablation and subsequent laser nanostructuring at room temperature has been employed to produce nanostructured Ni on SiO2 /Si substrates for catalytic growth of carbon nanotubes. The resultant nanostructured surface is seen to consist of nanometer sized hemispherical droplets whose mean diameter is controlled by the initial metal thickness, which in turn is readily controlled by the ...
متن کاملGrowth process conditions of vertically aligned carbon nanotubes using plasma enhanced chemical vapor deposition
The growth of vertically aligned carbon nanotubes using a direct current plasma enhanced chemical vapor deposition system is reported. The growth properties are studied as a function of the Ni catalyst layer thickness, bias voltage, deposition temperature, C2H2:NH3 ratio, and pressure. It was found that the diameter, growth rate, and areal density of the nanotubes are controlled by the initial ...
متن کاملStudy of electron eld emission from arrays of multi-walled carbon nanotubes synthesized by hot-wire dc plasma-enhanced chemical vapor deposition
Multi-walled carbon nanotubes have been grown on 7 nm Ni-coated substrates consisting of 300 lm thick highly n-doped (1 0 0) silicon covered with a di usion barrier layer (10 nm thick) of SiO2 or TiN, by combining hot-wire chemical vapor deposition and direct current plasma-enhanced chemical vapor deposition at low temperature (around 620 °C). Acetylene gas was used as carbon source and ammonia...
متن کاملStudy of electron field emission from arrays of multi-walled carbon nanotubes synthesized by hot-wire dc plasma-enhanced chemical vapor deposition
Multi-walled carbon nanotubes have been grown on 7 nm Ni-coated substrates consisting of 300 lm thick highly n-doped (1 0 0) silicon covered with a di usion barrier layer (10 nm thick) of SiO2 or TiN, by combining hot-wire chemical vapor deposition and direct current plasma-enhanced chemical vapor deposition at low temperature (around 620 °C). Acetylene gas was used as carbon source and ammonia...
متن کاملSynthesis of multi-walled carbon nanotubes by combining hot-wire and dc plasma-enhanced chemical vapor deposition
Multi-walled carbon nanotubes (MWCNTs) have been grown on 7 nm Ni-coated substrates consisting of crystalline silicon covered with a thin layer (10 nm) of TiN, by combining hot-wire chemical vapor deposition (HWCVD) and direct current plasma-enhanced chemical vapor deposition (dc PECVD), at 620 -C. Acetylene (C2H2) gas is used as the carbon source and ammonia (NH3) and hydrogen (H2) are used ei...
متن کامل