Measurement of the reversible hydrogen storage capacity of milligram Ti–6Al–4V alloy samples with temperature programmed desorption and volumetric techniques

نویسندگان

  • Jeff L. Blackburn
  • Philip A. Parilla
  • Thomas Gennett
  • Katherine E. Hurst
  • Anne C. Dillon
  • Michael J. Heben
چکیده

Measurement of the reversible hydrogen storage capacity of milligram Ti–6Al–4V alloy samples with temperature programmed desorption and volumetric techniques Jeff L. Blackburn a,∗, Philip A. Parilla a, Thomas Gennett b, Katherine E. Hurst c, Anne C. Dillon a, Michael J. Heben a a National Renewable Energy Laboratory, 1617 Cole Blvd, Golden, CO 80401, USA b Chemistry Department, Rochester Institute of Technology, Rochester, NY 14623, USA c National Institute of Standards, Boulder, CO 80305, USA

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Susceptibility to Hydrogen Absorption and Hydrogen Thermal Desorption of Titanium Alloys Immersed in Neutral Fluoride Solution under Applied Potential

The susceptibility to hydrogen absorption and hydrogen thermal desorption of titanium alloys has been investigated in a neutral 2.0% NaF solution at 37 C under various applied cathodic potentials. Ti-0.2Pd, Ti-6Al-4V and Ti-11.3Mo-6.6Zr-4.3Sn alloys absorb hydrogen under less noble potentials than 1:5V, 1:9V and 1:4V versus a saturated calomel electrode, respectively. The amounts of absorbed hy...

متن کامل

TIG Surface Alloying of Ti-6Al-4V with Nitrogen and Chromium for Improved Tribological Properties

Due to special properties such as low density, high strength and high corrosion resistance Ti-6Al-4V alloy has been used extensively in various industries, especially in the aerospace aspects. However the major problem of this alloy is its poor tribological properties under relatively high loads. In the present study, in order to improve the tribological properties of mentioned alloy, chromium ...

متن کامل

Microstructural Evaluation of Ti-6AL-4V Alloy during Hot Deformation

Among the titanium alloys, Ti-6Al-4V is the most widely used. In the present work, the uniaxial hot compressive behavior of Ti-6Al-4V has been investigated under constant strain rates. A series of dilatometery experiments were carried out to determine the transformation temperatures at different cooling rates. Specimens were homogenized at 1050 °C for 10 minutes followed by fast cooling to dif...

متن کامل

Investigation of the effect of temperature on the corrosion behavior of welded joints similar of titanium alloy Ti-6Al-4V by friction stir welding method

In this study, corrosion behavior of Ti-6Al-4V titanium alloy joint by friction stir welding with a rotational speed of 375 rpm and a travel speed of 100 mm/min was investigated. The welding procedure was carried out under β-transus temperature that was consisted of equiaxed grains in the stir zone. The corrosion behavior of the welded joint was investigated in 3.5% NaCl solution at temperature...

متن کامل

Microstructural Evaluation of Ti-6AL-4V Alloy during Hot Deformation

Among the titanium alloys, Ti-6Al-4V is the most widely used. In the present work, the uniaxial hot compressive behavior of Ti-6Al-4V has been investigated under constant strain rates. A series of dilatometery experiments were carried out to determine the transformation temperatures at different cooling rates. Specimens were homogenized at 1050 °C for 10 minutes followed by fast cooling to dif...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2008