Cells in Sol-Gels I: A Cytocompatible Route for the Production of Macroporous Silica Gels
نویسندگان
چکیده
A novel, high hydrolysis ratio sol-gel route for the biocompatible production of macroporous silica gels is presented. This route exploits the two step nature of the gelation reaction to remove undesired alcohol by-products from an acidic aqueous sol prior to gelation. These alcohol-free sols will gel when the pH is raised to the physiologic range in a two-step, acid/base catalyzed process. Furthermore, monolithic macroporous samples can be produced in a controlled manner by introducing water-soluble organic polymers into the sol.
منابع مشابه
Formation of bimodal porous silica-titania monoliths by sol-gel route
Silica-titania monoliths with micrometer-scale macroporous and nanometer-scale mesoporous structure and high titania contents are prepared by sol-gel process and phase separation. Titanium alkoxide precursor was not effective in the preparation of high titania content composites because of strong decrease in phase separation tendency. Bimodal porous gels with high titania content were obtained ...
متن کاملLipase Immobilized into Novel GPTMS: TMOS Derived Sol-Gels and Its Application for Biodiesel Production from Waste Oil
In this essay, lipase from Burkholderia cepacia was immobilized into 3-glycidoxypropyltrimethoxysilane (GPTMS) and tetramethoxysilane (TMOS) derived sol-gels. GPTMS:TMOS molar ratio of 1:3 was found to yield the best result. The morphological characteristics were investigated based on SEM and BET analysis. Sample mean pore diameter was 39.1 nm, it had a specific surface area of 60 m2/g prior to...
متن کاملPreparation and Characterization of ZrO2/TiO2 Nanocomposite under Ultrasonic Irradiation by Sol-gel Route
TiO2/ZrO2 nanocomposite was obtained by the sonochemical technique. In this method, two separate gels containing zirconium and titanium were prepared and mixed together. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4. The precursor titanium tetra isopropoxide (TTIP) dissolved in isopropanol. Mixing of Titanium and Zirconium gels was resulted in a yellow TiO2/ZrO2 ...
متن کاملPreparation and Characterization of ZrO2/TiO2 Nanocomposite under Ultrasonic Irradiation by Sol-gel Route
TiO2/ZrO2 nanocomposite was obtained by the sonochemical technique. In this method, two separate gels containing zirconium and titanium were prepared and mixed together. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4. The precursor titanium tetra isopropoxide (TTIP) dissolved in isopropanol. Mixing of Titanium and Zirconium gels was resulted in a yellow TiO2/ZrO2 ...
متن کاملPreparation and Characterization of ZrO2/ZnO Nanocomposite under Ultrasonic Irradiation via Sol-gel Route
Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...