Charge-induced reversible bending in nanoporous alumina-aluminum composite
نویسندگان
چکیده
منابع مشابه
Flexural Properties and Fracture Behavior of Nanoporous Alumina film by Three-Point Bending Test
This study investigated the influence of porosity on the flexural property of a nanoporous alumina film. When the porosity of the alumina film increased, both bending strength and modulus declined. The results from the bending test revealed that the setting of the film during the bending test had significant influence on the flexural property. Fracture only occurred when the porous side of the ...
متن کاملThermally Stable Nanoporous Gold-Alumina Core-Shell with Tunable Optical Transmission
Tuning localized surface plasmon resonance (LSPR) of nanoporous metals is crucial to manipulate light within tiny volumes for the implementation of optical devices at the nanoscale. Herein, nanoporous gold-alumina core-shell films with constant gold skeleton and variable alumina sheaths are fabricated by means of chemical corrosion and subsequent atomic layer deposition. Optical transmission pr...
متن کاملAnodization of nanoporous alumina on impurity-induced hemisphere curved surface of aluminum at room temperature
Nanoporous alumina which was produced by a conventional direct current anodization [DCA] process at low temperatures has received much attention in various applications such as nanomaterial synthesis, sensors, and photonics. In this article, we employed a newly developed hybrid pulse anodization [HPA] method to fabricate the nanoporous alumina on a flat and curved surface of an aluminum [Al] fo...
متن کاملStudy of Mechanical Properties for the Aluminum Bronze Matrix Composites of Hot Pressing
The aluminum bronze matrix alumina composites using hot press and resin infiltration were investigated to study their porosities, hardness, bending strengths, and microstructures. The experiment results show that the hardness of the sintered composites with the decrease of porosity increases. The composites without and with resin infiltration have about HRF 42-61 of about 34-40% of porosity and...
متن کاملPreparation and characterization of superhydrophobic surfaces based on hexamethyldisilazane-modified nanoporous alumina
Superhydrophobic nanoporous anodic aluminum oxide (alumina) surfaces were prepared using treatment with vapor-phase hexamethyldisilazane (HMDS). Nanoporous alumina substrates were first made using a two-step anodization process. Subsequently, a repeated modification procedure was employed for efficient incorporation of the terminal methyl groups of HMDS to the alumina surface. Morphology of the...
متن کامل