Tunability Limit of Photoluminescence in Colloidal Silicon Nanocrystals
نویسندگان
چکیده
Luminescent silicon nanocrystals (Si NCs) have attracted tremendous research interest. Their size dependent photoluminescence (PL) shows great promise in various optoelectronic and biomedical applications and devices. However, it remains unclear why the exciton emission is limited to energy below 2.1 eV, no matter how small the nanocrystal is. Here we interpret a nanosecond transient yellow emission band at 590 nm (2.1 eV) as a critical limit of the wavelength tunability in colloidal silicon nanocrystals. In the "large size" regime (d > ~3 nm), quantum confinement dominantly determines the PL wavelength and thus the PL peak blue shifts upon decreasing the Si NC size. In the "small size" regime (d < ~2 nm) the effect of the yellow band overwhelms the effect of quantum confinement with distinctly increased nonradiative trapping. As a consequence, the photoluminescence peak does not exhibit any additional blue shift and the quantum yield drops abruptly with further decreasing the size of the Si NCs. This finding confirms that the PL originating from the quantum confined core states can only exist in the red/near infrared with energy below 2.1 eV; while the blue/green PL originates from surface related states and exhibits nanosecond transition.
منابع مشابه
Surface charges and optical characteristic of colloidal cubic SiC nanocrystals
Colloidal cubic silicon carbide (SiC) nanocrystals with an average diameter of 4.4 nm have been fabricated by anisotropic wet chemical etching of microsized cubic SiC powder. Fourier transform infrared spectra show that these cubic SiC nanocrystals contain carboxylic acid, SiH, CH, and CHx groups. UV/Vis absorption and photoluminescence (PL) spectroscopy clearly indicate that water and ethanol ...
متن کاملCationic Silicon Nanocrystals with Colloidal Stability, pH‐Independent Positive Surface Charge and Size Tunable Photoluminescence in the Near‐Infrared to Red Spectral Range
In this report, the synthesis of a novel class of cationic quaternary ammonium-surface-functionalized silicon nanocrystals (ncSi) using a novel and highly versatile terminal alkyl halide-surface-functionalized ncSi synthon is described. The distinctive features of these cationic ncSi include colloidal stability, pH-independent positive surface charge, and size-tunable photoluminescence (PL) in ...
متن کاملSilicon Nanocrystals: Cationic Silicon Nanocrystals with Colloidal Stability, pH‐Independent Positive Surface Charge and Size Tunable Photoluminescence in the Near‐Infrared to Red Spectral Range (Adv. Sci. 2/2016)
متن کامل
Synthesis of colloidal solutions with silicon nanocrystals from porous silicon
UNLABELLED In this work, we have obtained colloidal solutions of Si nanocrystals (Si-ncs), starting from free-standing porous silicon (PSi) layers. PSi layers were synthesized using a two-electrode Teflon electrochemical cell; the etching solution contained hydrogen peroxide 30%, hydrofluoric acid 40% (HF), and methanol. The anodizing current density was varied to 250 mA cm(-2), 1 A cm(-2), and...
متن کاملColor-stable water-dispersed cesium lead halide perovskite nanocrystals.
Cesium lead halide perovskite nanocrystals are being lately explored for optoelectronic applications due to their emission tunability, high photoluminescence quantum yields, and narrow emission bands. Nevertheless, their incompatibility with polar solvents and composition homogenization driven by a fast anion-exchange are still important drawbacks to overcome. Herein we report on a successful e...
متن کامل