Weak localization and electron-electron interactions in polycrystalline tin dioxide films
نویسندگان
چکیده
Electrical and magnetotransport properties of polycrystalline tin dioxide films were investigated in the temperature range 2-300 K and in high magnetic fields up to 27 T. The experimental data were analyzed using models inherent both for 2D and 3D disordered systems. A crossover from 2D to 3D behaviour was observed as the temperature was increased.
منابع مشابه
Characterization of Ito Thin Films Prepared by Spinning Deposition Starting from a Sol-gel Process
ITO thin films were deposited by spin coating method starting from indium and tin propoxide in the frame of a sol-gel process. Films with the thickness corresponding to 68 nm for one layer deposition were produced and characterized by X-ray diffraction, transmission electron microscopy and infrared reflection spectroscopy. Low conductivity polycrystalline films exhibiting cubical structure (bix...
متن کاملStudies on tin oxide films prepared by electron beam evaporation and spray pyrolysis methods
Transparent conducting tin oxide thin films have been prepared by electron beam evaporation and spray pyrolysis methods. Structural, optical and electrical properties were studied under different preparation conditions like substrate temperature, solution flow rate and rate of deposition. Resistivity of undoped evaporated films varied from 2⋅65 × 10 Ω-cm to 3⋅57 × 10 Ω-cm in the temperature ran...
متن کاملEnhanced Physical Properties Of Indium Tin Oxide Films Grown on Zinc Oxide-Coated Substrates
Structural, electrical and optical properties of indium tin oxide or ITO (In2O3:SnO2) thin films on different substrates are investigated. A 100-nm-thick pre-deposited zinc oxide (ZnO) buffer layer is utilized to simultaneously improve the electrical and optical properties of ITO films. High purity ZnO and ITO layers are deposited with a radio frequency sputtering in argon ambient with plasma p...
متن کاملStructural and optical properties of ITO/TiO2 anti-reflective films for solar cell applications
Indium tin oxide (ITO) and titanium dioxide (TiO2) anti-reflective coatings (ARCs) were deposited on a (100) P-type monocrystalline Si substrate by a radio-frequency (RF) magnetron sputtering. Polycrystalline ITO and anatase TiO2 films were obtained at room temperature (RT). The thickness of ITO (60 to 64 nm) and TiO2 (55 to 60 nm) films was optimized, considering the optical response in the 40...
متن کاملEffect of substrate temperature on physical properties of In2O3:Sn films deposited by e-beam technique
Indium tin oxide (ITO) thin films were prepared by electron beam evaporation at different substrate temperatures. The structural studies were carried out by X-ray diffraction. Optical properties of the films were studied in the ultraviolet-visible-near infrared (UV-Vis-NIR) region (200 to 2500 nm). Electrical studies were carried out at room temperature of ITO films. The results showed that wit...
متن کامل