Effect of multiple debonding sequences on shear bond strength of new stainless steel brackets

OBJECTIVES This in-vitro study aimed at evaluating the effect of three debonding sequences on the shear bond strength (SBS) of new stainless steel (SS) brackets. MATERIALS AND METHODS Stainless steel twin brackets (0.022-inch, American Orthodontics, Sheboygan, WI, USA) were bonded with light cure adhesive (Transbond XT, 3M Unitek, St. Paul, MN, USA) to 80 newly extracted human premolars after acid etching with 37% phosphoric acid (30 s). Brackets were debonded with a universal testing machine, and new brackets were bonded to teeth using the same adhesive and same manner. This process was repeated twice, and brackets were debonded within 24 h after bonding. The longitudinal changes of average SBS were assessed with the repeated measures ANOVA. Post-hoc tests using the Bonferroni correction were also used to compare the average SBS at three debonding sequences. RESULT The mean SBS decreased significantly after each debonding sequence (P < 0.01). The corresponding mean values (standard deviation, 95% CI) after the first, second, and third debonding sequences were 22.88 MPa (4.08, 21.97-22.79), 19.36 MPa (4.54, 18.62-20.64), and 16.67 MPa (4.27, 15.72-17.62), respectively. There was no significant difference among the adhesive remnant index (ARI) scores of three debonding sequences (χ(2)= 5.067, df = 6, P = 0.53). CONCLUSION Average SBS after three debonding sequences was significantly decreased, but was above the recommended 5.9-7.8 MPa. In-vivo studies are required to validate the finding of this study.