Complete suppression of boron transient-enhanced diffusion and oxidation-enhanced diffusion in silicon using localized substitutional carbon incorporation
نویسندگان
چکیده
In this letter, we show the ability, through introduction of a thin Si12x2yGexCy layer, to eliminate the enhancement of enhanced boron diffusion in silicon due to an oxidizing surface or ion implant damage. This reduction of diffusion is accomplished through a low-temperature-grown thin epitaxial Si12x2yGexCy layer which completely filters out excess interstitials introduced by oxidation or ion implant damage. We also quantify the oxidation-enhanced diffusion ~OED! and transient-enhanced diffusion ~TED! dependence on substitutional carbon level, and further report both the observation of carbon TED and OED, and its dependence on carbon levels. © 1998 American Institute of Physics. @S0003-6951~98!00651-2#
منابع مشابه
Suppression of boron transient enhanced diffusion in SiGe heterojunction bipolar transistors by carbon incorporation
In this work, we demonstrate that the incorporation of carbon in the base of a npn Si/SiGe/Si heterojunction bipolar transistor dramatically reduces the outdiffusion of boron from the base under postgrowth implantation and annealing procedures. Without the addition of C, these processes would lead to transistors with vastly degraded transistor characteristics. This reduction in B diffusion, whe...
متن کاملDiffusion-limited interaction of dislocation loops and interstitials during dry oxidation in silicon
The interaction of implantation-induced dislocation loops and interstitials in silicon is studied. Experiments under dry oxidation conditions consistently show a significant reduction of OED (oxidation enhanced diffusion) of boron in a buried layer due to very efficient interstitial capturing action of dislocation loops, suggesting diffusion-limited dislocation loop growth. Simple analytic solu...
متن کاملPoint defect based modeling of low dose silicon implant damage and oxidation effects on phosphorus and boron diffusion in silicon
Point defect kinetics are important for understanding and modeling dopant diffusion in silicon. This article describes point defect models and compares them with experimental results for intrinsically doped material. Transient dopant diffusion due to low dose silicon implant damage can be modeled with the same parameters as oxidation enhanced diffusion, and therefore provides an additional tech...
متن کاملA comparison of boron and phosphorus diffusion and dislocation loop growth from silicon implants into silicon
Transient enhanced diffusion �TED� results from implantation damage creating enhanced diffusion of dopants in silicon. This phenomenon has mostly been studied using boron marker layers. We have performed an experiment using boron, phosphorus, and dislocation markers to compare TED effects. This experiment shows that phosphorus is enhanced significantly more than boron during damage annealing. D...
متن کاملBoron Segregation in Single-Crystal Si1−x−yGexCy and Si1−yCy Alloys
It has been reported that boron segregates to single-crystal Si1−xGex layers from silicon during thermal anneals. In this work, we find that boron segregates even more strongly into single-crystal Si1−x−yGexCy, as has been previously reported for polycrystalline films. This effect is also observed in single-crystal Si1−yCy. Segregation coefficients range from 1.7 to 2.9 for annealing temperatur...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 1998