Preparation and Characterization of Bioplastic-Based Green Renewable Composites from Tapioca with Acetyl Tributyl Citrate as a Plasticizer
نویسندگان
چکیده
Granular tapioca was thermally blended with poly(lactic acid) (PLA). All blends were prepared using a plasti-corder and characterized for tensile properties, thermal properties and morphology. Scanning electron micrographs showed that phase separation occurred, leading to poor tensile properties. Therefore, methylenediphenyl diisocyanate (MDI) was used as an interfacial compatibilizer to improve the mechanical properties of PLA/tapioca blends. The addition of MDI could improve the tensile strength of the blend with 60 wt% tapioca, from 19.8 to 42.6 MPa. In addition, because PLA lacked toughness, acetyl tributyl citrate (ATBC) was added as a plasticizer to improve the ductility of PLA. A significant decrease in the melting point and glass-transition temperature was observed on the basis of differential scanning calorimetry, which indicated that the PLA structure was not dense after ATBC was added. As such, the brittleness was improved, and the elongation at break was extended to several hundred percent. Therefore, mixing ATBC with PLA/tapioca/MDI blends did exhibit the effect of plasticization and biodegradation. The results also revealed that excessive plasticizer would cause the migration of ATBC and decrease the tensile properties.
منابع مشابه
Preparation and Characterization of Novel Bionanocomposite Based on Tapioca Starch/Gelatin/Nanorod-rich ZnO: Towards Finding Antimicrobial Coating for Nuts
The effects of zinc oxide nanorod on the barrier, sorption isotherm and antibacterial properties of tapioca starch/bovine gelatin Bionanocomposite films were investigated. The nanorod-rich ZnO (ZnO-N) was homogenized by sonication and incorporated into tapioca starch/bovine gelatin solutions at different concentrations (e.g. 0.5, 2, and 3.5% w/w dried solid). Incorporation of 3.5% of nanopartic...
متن کاملThe Effect of Additives Interaction on the Miscibility and Crystal Structure of Two Immiscible Biodegradable Polymers
Poly lactic acid (PLLA) is a promising biopolymer, obtained from polymerization of lactic acid that is derived from renewable resources through fermentation. The characteristic brittleness of PLLA is attributed to slow crystallization rates, which results in the formation of the large spherulites. Its glass temperature is relative high, above room temperature and close to 60 °C, and therefore i...
متن کاملPreparation and Characterization of Pullulan-Soy Protein Concentrate Biocomposite Film
The non-biodegradable nature of plastic packaging has brought about an attention in bio-basedpackaging materials. Edible composite films were prepared using soy protein concentrate (SPC) and pullulan(PUL) biopolymer at five different ratio (100:0; 70:30; 50:50; 30:70 and 0:100) with glycerol as plasticizer bycasting-evaporation method. The thickness, mechanical properties, water vapor permeabil...
متن کاملProcessing Conditions, Thermal and Mechanical Responses of Stretchable Poly (Lactic Acid)/Poly (Butylene Succinate) Films
Poly (lactic acid) (PLA) and poly (butylene succinate) (PBS) based films containing two different plasticizers [Acetyl Tributyl Citrate (ATBC) and isosorbide diester (ISE)] at three different contents (15 wt %, 20 wt % and 30 wt %) were produced by extrusion method. Thermal, morphological, mechanical and wettability behavior of produced materials was investigated as a function of plasticizer co...
متن کاملCytocompatibility of new phthalate ester-free tissue conditioners in vitro.
The estrogenic activity of phthalate esters for dental use as plasticizers was concerned. To study the feasibility of candidate chemicals for phthalate tissue conditioners, three candidate plasticizers, di-n-butyl sebacate, acetyl tributyl citrate and tri-n-butyl phosphate together with conventional plasticizers were examined for estrogenic activity and cytotoxicity using three estrogenicity as...
متن کامل