Thermodynamics and kinetics of the undercooled liquid and the glass transition of the Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 alloy
نویسندگان
چکیده
Differential scanning calorimetry (DSC) was used to determine the thermodynamic functions of the undercooled liquid and the amorphous phase with respect to the crystalline state of the ~41.2Ti13.8CU125Nilo.OBe22.5 bulk mltallic glass forming alloy. The specific heat capacities of this alloy. in the undercooled liquid, the amorphous state and the crystal were determined. The differences in enthalpy, AH, entropy, AS, and Gibbs free energy, AG, between crystal and the undercooled liquid were calculated using the measured specific heat capacity data as well as the heat of fusion. The results indicate that the Gibbs free energy difference between metastable undercooled liquid and crystalline solid, AG, stays small compared to conventional metallic glass forming alloys even for large undercoolings. Furthermore, the Kauzmann temperature, TK, where the entropy of the undercooled liquid equals to that of the crystal, was determined to be 560 K. The Kauzmann temperature is compared with the experimentally observed rate-dependent glass transition temperature, TR. Both onset and end temperatures of the glass transition depend linearly on the logarithm of the heating rate based on the DSC experiments. Those characteristic temperatures for the kinetically observed glass transition become equal close to the Kauzmann temperature in this alloy, which suggests an underlying thermodynamic glass transition as a lower bound for the kinetically observed freezing process.
منابع مشابه
Hemispherical total emissivity and specific heat capacity of deeply undercooled Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 melts
High-temperature high-vacuum electrostatic levitation ~HTHVESL! and differential scanning calorimetry ~DSC! were combined to determine the hemispherical total emissivity eT , and the specific heat capacity cp , of the undercooled liquid and throughout the glass transition of the Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 bulk metallic glass forming alloy. The ratio of cp /eT as a function of undercooling w...
متن کاملExperimental determination of a time–temperature-transformation diagram of the undercooled Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 alloy using the containerless electrostatic levitation processing technique
High temperature high vacuum electrostatic levitation was used to determine the complete time– temperature–transformation ~TTT! diagram of the Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 bulk metallic glass forming alloy in the undercooled liquid state. This is the first report of experimental data on the crystallization kinetics of a metallic system covering the entire temperature range of the undercooled ...
متن کاملDecomposition and primary crystallization in undercooled Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 melts
Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 bulk metallic glasses were prepared by cooling the melt with a rate of about 10 K/s and investigated with respect to their chemical and structural homogeneity by atom probe field ion microscopy and transmission electron microscopy. The measurements on these slowly cooled samples reveal that the alloy exhibits phase separation in the undercooled liquid state. Signi...
متن کاملMetallic glass formation in highly undercooled Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 during containerless electrostatic levitation processing
Various sample sizes of Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 with masses up to 80 mg were undercooled below Tg ~the glass transition temperature! while electrostatically levitated. The final solidification product of the sample was determined by x-ray diffraction to have an amorphous phase. Differential scanning calorimetry was used to confirm the absence of crystallinity in the processes sample. The...
متن کاملDendrite Growth Kinetics in Undercooled Melts of Intermetallic Compounds
Solidification needs an undercooling to drive the solidification front. If large undercoolings are achieved, metastable solid materials are solidified from the undercooled melt. Containerless processing provides the conditions to achieve large undercoolings since heterogeneous nucleation on container walls is completely avoided. In the present contribution both electromagnetic and electrostatic...