Comparative study of thermally cured and electron-beam-exposed hydrogen silsesquioxane resists
نویسندگان
چکیده
A comparative study of the changes in the chemical structure and properties of hydrogen silsesquioxane HSQ resists induced by thermal curing and electron-beam exposure has been conducted. Studies using Fourier transform infrared FTIR spectroscopy suggested similar behavior in the redistribution of bonds for both processes. Quantitative analysis of both spectra revealed the existence of a critical temperature and electron dose for the achievement of development for pattern generation. As a complementary technique, x-ray reflectivity measurements were performed to monitor changes in the film density. Notwithstanding the similar changes in bond redistribution observed from the FTIR spectra for both thermal curing and electron-beam exposure, the film densification processes seem to occur in quite distinctive fashions. This was confirmed through dry etching experiments; the results of which were consistent for both Freon and Cl2 /Ar reactive ion etching. While effective film densification occurred only at curing temperatures above 400 °C, insignificant changes in density and etch durability were observed for electron-beam-exposed HSQ resists at electron doses commonly used for pattern generation. Wet etching characteristics engendered by hydrofluoric acid showed that both chemical bond redistribution and densification lead to decreases in etch rates. © 2008 American Vacuum Society. DOI: 10.1116/1.2960565
منابع مشابه
Electron-beam exposure mechanisms in hydrogen silsesquioxane investigated by vibrational spectroscopy and in situ electron-beam-induced desorption
Hydrogen silsesquioxane HSQ is used as a high-resolution resist with resolution down below 10 nm half-pitch. This material or materials with related functionalities could have widespread impact in nanolithography and nanoscience applications if the exposure mechanism was understood and instabilities controlled. Here we have directly investigated the exposure mechanism using vibrational spectros...
متن کاملSub-10-nm half-pitch electron-beam lithography by using poly(methyl methacrylate) as a negative resist
Developing high-resolution resists and processes for electron-beam lithography is of great importance for high-density magnetic storage, integrated circuits, and nanoelectronic and nanophotonic devices. Until now, hydrogen silsesquioxane HSQ and calixarene were the only two reported negative resists that could approach sub-10-nm half-pitch resolution for electron-beam lithography. Here, the aut...
متن کاملEnhancing etch resistance of hydrogen silsesquioxane via postdevelop electron curing*
In this work, the authors enhanced the etch resistance of the negative-tone electron resist, hydrogen silsesquioxane HSQ to CF4 reactive ion etching RIE by curing HSQ after development. They fabricated superconducting nanowires that were 15 nm wide by pattern transfer into a 6-nm-thick layer of NbN using cured HSQ as the etch mask. HSQ was cured using a postdevelop electron-beam exposure step p...
متن کاملSub-5 keV Electron-Beam Lithography in Hydrogen Silsesquioxane Resist
We fabricated 9 to 30 nm half-pitch nested Ls and 13 to 15 nm half-pitch dot arrays, using 2 keV electron-beam lithography with hydrogen silsesquioxane (HSQ) as the resist. All structures with 15 nm half-pitch and above were fully resolved. We observed that the 9 and 10-nm half-pitch nested L’s and the 13-nm-half-pitch dot array contained some resist residues. We obtained good agreement between...
متن کاملThree-dimensional nanofabrication using HSQ/PMMA bilayer resists
Citation Do, Hyung Wan, Jae-Byum Chang, and Karl K. Berggren. “Three-Dimensional Nanofabrication Using Hydrogen Silsesquioxane/poly(methylmethacrylate) Bilayer Resists.” Journal of Vacuum Science & Technology B, Nanotechnology and Microelectronics: Materials, Processing, Measurement, and Phenomena 32, no. 6 (November 2014): 06F501. As Published http://dx.doi.org/10.1116/1.4893659 Publisher Amer...