Cleavage cracking across triple grain boundary junctions in freestanding silicon thin films
نویسندگان
چکیده
This article is focused on a fractography study of cleavage cracking at triple grain boundary junctions in freestanding silicon thin films. At a triple junction, as the crystallographic orientations of the two grains ahead of the crack are different by only a few degrees, the cleavage front advance becomes quite jerky. The crack first enters the grain of smaller boundary toughness and then turns into the other grain from the lateral direction. Consequently, the overall fracture resistance cannot be analyzed in the framework of line-average theory. The nonuniform characteristic of crack behavior can be attributed to the increase in local stress intensity. A few typical crack front advance modes are identified.
منابع مشابه
Resistance of grain boundary array to cleavage cracking in free-standing thin film
In a previous experimental study on free-standing silicon thin film, it was observed that cleavage front transmission across a through-thickness grain boundary could be considerably constrained by film surfaces. As a result, the boundary toughness was much lower than its bulk counterpart. In this study, inspired by the observation of crack front behaviors at triple grain boundary junctions, we ...
متن کاملCleavage cracking across twin boundaries in free-standing silicon thin films
Cleavage cracking across twin boundaries in freestanding silicon thin films is investigated in a microtensile fracture experiment. If the twist misorientation is relatively small, the crack front transmission can be quite smooth; otherwise the fracture surface may be either planar or broken down into parallel terrains. In all the cases, the local fracture resistance tends to increase. PACS 62.2...
متن کاملEnergy equilibrium of cleavage front transmission across a high-angle grain boundary in a free-standing silicon thin film
In this article, the crack growth driving force and the resistance to cleavage cracking associated with crack front transmission across a high-angle grain boundary in a silicon thin film are analyzed, and a closed-form solution of grain boundary toughness is obtained. It is noticed that the fracture resistance of the grain boundary is a function of the film thickness. This size effect is attrib...
متن کاملSecondary cracking at grain boundaries in silicon thin films
In this article, we report irregular cleavage front transmission at grain boundaries in free-standing polysilicon thin films. When the orientations of two adjacent grains are correlated, the crack may bypass the boundary via a ‘‘tunneling’’ process. Similar behavior can also be achieved if the crack path curves in the grain-boundary-affected zone. Moreover, the separation of crack flanks can be...
متن کاملResistance of through-thickness grain boundaries to cleavage cracking in silicon thin films
Through a set of microtensile experiments, it was discovered that the resistance of a free-standing polycrystalline silicon thin film to cleavage cracking is not a material constant. Rather, it is highly dependent on the film thickness. As the film thickness changes from 1 to 10 lm, the fracture resistance increases by 20–60%, which can be attributed to the nonuniform nature of the crack front ...