Confinement effects on the shape and composition of bimetallic nano-objects in carbon nanotubes.
نویسندگان
چکیده
CoPt and FePt nanostructures have been efficiently confined in carbon nanotubes (CNTs). A marked confinement effect has been evidenced, both on bimetallic nano-object shape and composition. In large diameter CNTs small Co- and Fe-rich nanoparticles are formed, while in small diameter CNTs Pt-rich nanowires are selectively produced.
منابع مشابه
Effects of Confinement in Carbon Nanotubes on the Performance and Lifetime of Fischer-Tropsch Iron Nano Catalysts
The effects of confinement in carbon nanotubes on Fischer-Tropsch (FT) activity, selectivity and lifetime of Carbon NanoTubes (CNTs) supported iron catalysts are reported. A method was developed to control the position of the catalytic sites on either inner or outer surface of carbon nanotubes. TEM analyses revealed that more than 80% of iron oxide particles can be controlled to be position...
متن کاملGrowth of CNTs over Fe–Co/Nanometric TiO2 Catalyst by CVD: The Effects of Catalyst Composition and Growth Temperature
In this research carbon nanotubes were produced by chemical vapor deposition of acetylene over a mixture of iron and cobalt catalysts supported on nanometric TiO2 and the influences of two synthesis parameters: growth temperature and catalyst composition ratio on properties of end-product carbon nanotubes were investigated. The catalytic basis was prepared by wet impregnation ...
متن کاملRole of growth temperature in CVD synthesis of Carbon nanotubes from Ni-Co bimetallic catalysts
The effect of temperature variation on the growth of Carbon Nanotubes (CNTs) using Thermal Chemical Vapor Deposition (TCVD) is presented. Nickel and Cobalt (Ni-Co) thin films on Silicon (Si) substrates were used as catalysts in TCVD technique. Acetylene gas was used in CNTs growth process at the controlled temperature ranges from 850-1000 ̊ C. Catalysts and CNTs characterization was carried out ...
متن کاملRole of growth temperature in CVD synthesis of Carbon nanotubes from Ni-Co bimetallic catalysts
The effect of temperature variation on the growth of Carbon Nanotubes (CNTs) using Thermal Chemical Vapor Deposition (TCVD) is presented. Nickel and Cobalt (Ni-Co) thin films on Silicon (Si) substrates were used as catalysts in TCVD technique. Acetylene gas was used in CNTs growth process at the controlled temperature ranges from 850-1000 ̊ C. Catalysts and CNTs characterization was carried out ...
متن کاملMonodisperse pattern nanoalloying for synergistic intermetallic catalysis.
Nanoscale alloys attract enormous research attentions in catalysis, magnetics, plasmonics and so on. Along with multicomponent synergy, quantum confinement and extreme large surface area of nanoalloys offer novel material properties, precisely and broadly tunable with chemical composition and nanoscale dimension. Despite substantial progress of nanoalloy synthesis, the randomized positional arr...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 52 11 شماره
صفحات -
تاریخ انتشار 2016