Comparative study of mechanical properties of dental restorative materials and dental hard tissues in compressive loads

نویسندگان

  • Keyoung Jin Chun
  • Jong Yeop Lee
چکیده

There are two objectives. One is to show the differences in the mechanical properties of various dental restorative materials compared to those of enamel and dentin. The other is to ascertain which dental restorative materials are more suitable for clinical treatments. Amalgam, dental ceramic, gold alloy, dental resin, zirconia, and titanium alloy were processed as dental restorative material specimens. The specimens (width, height, and length of 1.2, 1.2, and 3.0 mm, respectively) were compressed at a constant loading speed of 0.1 mm/min. The maximum stress (115.0 ± 40.6, 55.0 ± 24.8, 291.2 ± 45.3, 274.6 ± 52.2, 2206.0 ± 522.9, and 953.4 ± 132.1 MPa), maximum strain (7.8% ± 0.5%, 4.0% ± 0.1%, 12.7% ± 0.8%, 32.8% ± 0.5%, 63.5% ± 14.0%, and 45.3% ± 7.4%), and elastic modulus (1437.5 ± 507.2, 1548.4 ± 583.5, 2323.4 ± 322.4, 833.1 ± 92.4, 3895.2 ± 202.9, and 2222.7 ± 277.6 MPa) were evident for amalgam, dental ceramic, gold alloy, dental resin, zirconia, and titanium alloy, respectively. The reference hardness value of amalgam, dental ceramic, gold alloy, dental resin, zirconia, and titanium alloy was 90, 420, 130-135, 86.6-124.2, 1250, and 349, respectively. Since enamel grinds food, its abrasion resistance is important. Therefore, hardness value should be prioritized for enamel. Since dentin absorbs bite forces, mechanical properties should be prioritized for dentin. The results suggest that gold alloy simultaneously has a hardness value lower than enamel (74.8 ± 18.1), which is important in the wear of the opposing natural teeth, and higher maximum stress, maximum strain, and elastic modulus than dentin (193.7 ± 30.6 MPa, 11.9% ± 0.1%, 1653.7 ± 277.9 MPa, respectively), which are important considering the rigidity to absorb bite forces.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Comparative Evaluation of Surface Hardness of Different Resin-Modified Glass Ionomers and a Compomer

Introdouction: Due to the practical problems and time restriction issues in treating dental problems in children, there is a noticeable demand for the application of a convenient handling restorative material with acceptable physical-mechanical properties. The aim of this investigation was to evaluate Vickers microhardness of four tooth-colored restorative materials as a determining mechanical...

متن کامل

Compressive Properties of Enamel , Dental Cements , and Gold

The compressive properties of human enamel and dentin have been reported by Stanford, Paffenbarger, Kumpula, and Sweeney.' The elastic modulus of occlusal, side, and cusp enamel was reported to be 1.8, 6.0, and 8.2 X 106 psi, respectively. The corresponding values for the proportional limit were 16,800, 21,000, and 34,200 psi and, for the compressive strength, 19,400, 28,300, and 40,200 psi. An...

متن کامل

Improving mechanical properties of glass ionomer cements with fluorhydroxyapatite nanoparticles

Glass ionomer cements show great potential as low cost, minimally invasive dental restorative materials. However, their use is limited by relatively poor mechanical properties, especially fracture toughness. One possibility for improving their fracture toughness is through the addition of fluorhydroxyapatite nanoparticles, which resemble the crystals found in tooth enamel. Hydroxyapatite and fl...

متن کامل

Evaluation of Mechanical Properties of Flowable Dental Composites Containing Antibacterial Compound

Abstract   Background and Aims: The purpose of this study was to evaluate the mechanical properties of flowable dental composites containing the antibacterial compound. Materials and Methods: The study was conducted through experimental design. Compound 3- (2,5-Dimethylfuran-3-yl) -1H-pyrazol-5- (4H)-one were synthesized using Ethyl chloroformate, hydrazine hydrate and 3-acetyl-2,5-dimethylfur...

متن کامل

INVESTIGATING THE PHYSICAL AND MECHANICAL PROPERTIES OF HIGH-COPPER AND SILVER DENTAL-FILLING AMALGAM ALLOYS

Abstract: The aim of the present investigation is to study the physical and mechanical characteristics of dental-filling spherical high-copper and silver amalgams and to compare them with a common high-copper domestic unicompositional amalgam. In this study, cylindrical specimens were mechanically condensed according to the ISO 1559:1986 Standard in order to measure the compressive strength, Vi...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 5  شماره 

صفحات  -

تاریخ انتشار 2014