Synthesis of Porous NiO and ZnO Submicro- and Nanofibers from Electrospun Polymer Fiber Templates
نویسندگان
چکیده
Porous nickel oxide (NiO) and zinc oxide (ZnO) submicro- and nanofibers were synthesized by impregnating electrospun polyacrylonitrile (PAN) fiber templates with corresponding metal nitrate aqueous solutions and subsequent calcination. The diameter of the NiO and ZnO fibers was closely related to that of the template fibers and larger diameters were obtained when using the template fibers with larger diameter. SEM results showed that the NiO and ZnO fibers have a large amount of pores with diameters ranging from 5 nm to 20 nm and 50 nm to 100 nm, respectively. Energy dispersive X-ray (EDX) spectra and X-ray diffraction (XRD) patterns testified that the obtained materials were NiO and ZnO with high purity.
منابع مشابه
Fabrication, characterization, and microscopic imaging of Fe2O3-modified electrospun nanofibers
This study explored the fabrication, characterization, and microscopic imaging of highly porous electrospun nanofibers based on pure and Fe2O3 nanoparticle modified polyacrylonitrile (PAN) fibers. The desired electrospinning mixture comprising polymer and nanoparticles in dimethyleformamide, was prepared. During electrospinning, the precursor solution was injected using a ...
متن کاملSynthesis of Polypyrrole Coated SnO2-ZnO Electrospun Nanofibers via Vapor Phase Polymerization Method
This paper reports the synthesis of polypyrrole coated SnO2/ZnOelectrospunnanofibers via vapor phase polymerization method. In order to prepare one dimensional (SnO2- ZnO)/polypyrrole with the core sheath structure, first SnO2-ZnO composite nanofibers were synthesized via electrospinning method followed by adsorption of Fe 3+ on the surface of the SnO2-ZnO nanofibers and finally pyrrole w...
متن کاملCatalytically Graphitized Electrospun Carbon Nanofibers Adorned with Nickel Nanoparticles for Catalysis Applications
Catalytically graphitized electrospun carbon nanofibers adorned uniformly with fine nickel nanoparticles were successfully prepared. The procedure was based on the electrospinning technique and the use of nickel precursor to create both graphitized nanofibers and nickel nanoparticles under a relatively low-temperature heat treatment. The X-ray diffraction and Raman results clearly proved cataly...
متن کاملThe Review on Electrospun Gelatin Fiber Scaffold
The fabrication of the Guided Tissue Regeneration (GTR) membrane materials have become the key technique of the tissue engineering scaffold study. The cells adhere well on the fibers whose dimension is below their own so that the porous three dimension scaffold material can mimic the strueture of the natural extracellular matrix better and have the potential to be an ideal GTR membrane material...
متن کاملWater-soluble non-polymeric electrospun cyclodextrin nanofiber template for the synthesis of metal oxide tubes by atomic layer deposition
We report on the suitability of water-soluble non-polymeric electrospun cyclodextrin (CD) nanofiber templates by using atomic layer deposition (ALD) to yield metal oxide tubes. To demonstrate this, watersoluble electrospun CD nanofibers were chosen as template to produce metal oxide tubes where we have tested two examples of ALD coatings, namely, Al2O3 and ZnO. After the ALD coating on the CD n...
متن کامل