Effect of acidic primers on bonding three magnetic steel alloys with tri-n-butylborane initiated methacrylic resin.
نویسندگان
چکیده
The purpose of this study was to evaluate the effect of acidic primers on bonding magnetic steel alloys. Three alloys (XM27, 447J1, and AUM20) were primed with one of the following materials: Acryl Bond, Estenia Opaque Primer, Eye Sight Opaque Primer, M. L. Primer, or Super-Bond liquid. The specimens were bonded with a tri-n-butylborane initiated resin, and bond strength was determined both before and after thermocycling in water. Unprimed specimen was considered as the control. Average bond strength varied from 0 to 45.3 MPa for the XM27 alloy, 0.3 to 43.6 MPa for the 447J1 alloy, and 0.5 to 41.1 MPa for the AUM20 alloy. Of the five primers, Estenia Opaque Primer exhibited better adhesive performance than the other materials regardless of the type of steel alloy. It can be concluded that the use of the Estenia Opaque Primer, which contains an adhesive monomer (10-methacryloyloxydecyl dihydrogen phosphate; MDP), is recommended for bonding the three magnetic steel alloys with TBB-initiated resin.
منابع مشابه
Effect of acidic primers on adhesive bonding of tri-n-butylborane initiated adhesive resin to alumina.
The present study was conducted to evaluate the effect of acidic primers on adhesive bonding to sintered alumina. Alumina disk specimens were primed with one of the following acidic materials: Acryl Bond, All Bond II Primer B, Alloy Primer, Estenia Opaque Primer, Eye Sight Opaque Primer, M.L. Primer, MR. Bond, and Super-Bond Liquid. The disks were bonded with an adhesive resin (Super-Bond) init...
متن کاملEffect of single-liquid priming agents on adhesive bonding to aluminum oxide of a methacrylic resin.
The purpose of this study was to evaluate the effects of acidic primers on adhesive bonding to sintered aluminum oxide (alumina). Alumina disks were primed with one of the following materials: Acryl Bond, All Bond 2 Primer B, Alloy Primer, Estenia Opaque Primer, Eye Sight Opaque Primer, M.L. Primer, MR. Bond, and Super-Bond Liquid. Specimens were then bonded with an acrylic resin initiated with...
متن کاملBonding and wear characteristics of a tri-n-butylborane initiated adhesive resin filled with pre-polymerized composite particles.
This study evaluated the wear characteristics and bonding to silver-palladium-copper-gold (Ag-Pd-Cu-Au) alloy of an acrylic resin that was filled with pre-polymerized composite particles and initiated with tri-n-butylborane (TBB) derivative (Bondfill). Three methyl methacrylate (MMA)-based resins (Bondfill, Super-Bond, and Multi-Bond II) and a microfilled composite restorative material (Metafil...
متن کاملEvaluation of thiouracil-based adhesive systems for bonding cast silver-palladium-copper-gold alloy.
This study aimed to evaluate the effect of adhesive systems based on a thiouracil monomer on bonding to silver-palladium-copper-gold (Ag-Pd-Cu-Au) alloy (Castwell M.C.12). Disk specimens were cast from the alloy and then air-abraded with alumina. The disks were bonded using six bonding systems selected from four primers and three luting materials. Shear bond strengths were determined both befor...
متن کاملEffect of sodium sulfite, carboxylic monomer, and phosphoric acid etching on bonding of tri-n-butylborane initiated resin to human enamel.
The purpose of the present study is evaluation of bonding durability of tri-n-butylborane (TBB) initiated resin without 4-methacryloyloxyethyl trimellitate anhydride (4-META) joined to human enamel. Ground human enamel was bonded with TBB resin under six surface conditions: 1) as ground, 2) primed with Teeth Primer, 3) sodium sulfite solution, 4) 4-META solution, 5) acetone-water, and 6) phosph...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Dental materials journal
دوره 24 4 شماره
صفحات -
تاریخ انتشار 2005