Effects of sealant, viscosity, and bonding agents on microleakage of fissure sealants: An in vitro study

OBJECTIVE The aim of this study was to evaluate the effects of enamel or dentin bonding agent (DBA) and sealant viscosity on sealant microleakage. MATERIALS AND METHODS Sixty extracted human premolars were randomly divided into two equal groups (based on sealant viscosity) and each group was divided into three subgroups of 10 teeth. Group 1 (low viscosity sealant, Seal-Rite, Pulpdent, USA with 7.7% filler): Prophylaxis, enameloplasty, etching of occlusal surfaces with 38% of phosphoric acid gel, rinsing and drying, followed by (1) enamel bonding agent (EBA) (Margin Bond, Coltène/Whaledent AG) or (2) DBA (Excite, Ivoclar Vivadent AG, Liechtenstein) or (3) no bonding (NB) prior to sealant application. In Group 2, similar procedures were performed except for applying a high viscosity sealant (Seal-Rite, Pulpdent, The USA with 34.4% filler). Specimens were thermocycled and then immersed in a 0.5% basic fuchsine solution for 24 h next, buccolingual slices of samples were scored under a stereomicroscope. The Kruskal-Wallis and Mann-Whitney U-tests were used for data analysis. RESULTS There was no significant difference between DBA, EBA, and NB subgroups in the microleakage scores in both groups. Low viscosity sealant had a lower microleakage than the high viscosity sealant in both DBA (P = 0.002) and NB (P = 0.041) subgroups. CONCLUSION The results indicated that the use of low viscosity sealant reduced the microleakage of pit and fissure sealants. However, the use of a bonding agent before sealant placement didn't affect the microleakage.