Fracture Toughness of Advanced Ceramics at Room Temperature
نویسندگان
چکیده
This report presents the results obtained by the five U.S. participating laboratories in the Versailles Advanced Materials and Standards (VAMAS) round-robin for fracture toughness of advanced ceramics. Three test methods were used: indentation fracture, indentation strength, and single-edge pre-cracked beam. Two materials were tested: a gas-pressure sintered silicon nitride and a zirconia toughened alumina. Consistent results were obtained with the latter two test methods. Interpretation of fracture toughness in the zirconia alumina composite was complicated by R-curve and environmentally-assisted crack growth phenomena.
منابع مشابه
Toughness Scale from First Principles
We correlate the experimentally measured fracture toughness of 24 metals and ceramics to their quantum mechanically calculated brittleness parameter. The brittleness parameter is defined as the ratio of the elastic energy density needed to spontaneously break bonds in shear versus in tension, and is a primitive-cell property. Under 300 GPa hydrostatic pressure, the model predicts that diamond h...
متن کاملFracture toughness and thermal shock of tool and turbine ceramics
The behaviour of some commercial tool carbides and turbine ceramics has been investigated in regard to resistance to crack initiation, crack propagation and retained strength after thermal shock. New data are provided, particularly measurements of the fracture toughness of these materials at actual operating temperatures (up to 1200 ~ C). Many of the materials did not follow the generally accep...
متن کاملEffect of Silicon Carbide and graphite additives on the pressureless Sintering mechanism and microstructural characteristics of Ultra-High Temperature ZrB2 Ceramics Composites
The effect of SiC content, additives, and process parameters on densification and microstructural properties of pressureless sintered ZrB2– (1–10 wt %) SiC particulate composites have been studied. The ZrB2–SiC composite powders mixed by Spex mixer with 1-2wt% C (added as graphite powder) and CMC have been cold-compacted and sintered in argon environment in the temperature range of 1800–2100ºC ...
متن کاملTHERMAL FRACTURE OF CERAMICS WITH TEMPERATURE-DEPENDENT PROPERnES
Some aspects of thetmal fracture mechanics of ceramics with temperature-dependent properties are studied. It is first shown that the square-root singular field still prevaiLY in the crack tip region. However, the size of the K-dominant zone may be influenced by the effect of temperature-dependent properties. Then the steady thetmal stress intensity factor in an edge-cracked strip is calculated....
متن کاملSintering boron carbide ceramics without grain growth by plastic deformation as the dominant densification mechanism
A new ceramic sintering approach employing plastic deformation as the dominant mechanism is proposed, at low temperature close to the onset point of grain growth and under high pressure. Based on this route, fully dense boron carbide without grain growth can be prepared at 1,675-1,700 °C and under pressure of (≥) 80 MPa in 5 minutes. The dense boron carbide shows excellent mechanical properties...
متن کامل