Design of very transparent fluoropolymer resists for semiconductor manufacture at 157 nm
نویسندگان
چکیده
Photolithography at 157 nm requires development of new photoresists that are highly transparent at this wavelength. Transparent fluoropolymer platforms have been identified which also possess other materials properties required for chemically amplified imaging and aqueous development. Polymers of tetrafluoroethylene (TFE), a fluoroalcohol-substituted norbornene and an acid-labile acrylate ester show the best combination of properties. A solution, semibatch, free-radical polymerization process was developed allowing synthesis of the terpolymers on a multikilogram scale. Further property enhancements may arise from replacing the norbornene with functionalized tricyclononenes. Formulated resists have been imaged in a 157 nm microstepper. # 2003 Elsevier Science B.V. All rights reserved.
منابع مشابه
Single Layer Fluoropolymer Resists for 157 nm Lithography
We have developed a family of 157 nm resists that utilize fluorinated terpolymer resins composed of 1) tetrafluoroethylene (TFE), 2) a norbornene fluoroalcohol (NBFOH), and 3) t-butyl acrylate (t-BA). TFE incorporation reduces optical absorbance at 157 nm, while the presence of a norbornene functionalized with hexafluoroisopropanol groups contributes to aqueous base (developer) solubility and e...
متن کاملOptimizing polymers to increase pellicle lifetime and transmission for 157-nm lithography
The introduction of the 157-nm wavelength for next-generation optical lithography has created a need for new soft (polymeric) or hard (quartz) pellicle materials optimized for that wavelength. The design and development of ultratransparent fluoropolymers suitable for 157-nm soft-pellicle applications has produced several promising candidate materials with absorbances <0.03/μm to achieve pellicl...
متن کاملVisible-light photocatalytic activity of semiconductor composites supported by electrospun fiber
The preparation and photocatalysis of TiO2–ZnS/fluoropolymer fiber composites were investigated. The fluoropolymer nanofiber mats with carboxyl groups were prepared by electrospinning, and then titanium and zinc ions were introduced onto the fiber surfaces by the coordinating of carboxyl of fluoropolymer in solution. The TiO2–ZnS composites with diameters 15 nm to 1 lm were immobilized on the s...
متن کاملFluoropolymers for 157nm Lithography: Optical Properties from VUV Ellipsometry and Absorbance Measurements
With the introduction of 157 nm as the next optical lithography wavelength, the need for new pellicle and photoresist materials optimized for this wavelength has produced much activity in optical characterization of thin film materials. Here we focus on ultratransparent fluoropolymers for 157 nm pellicle applications where absorbances below 0.01/μm are necessary to achieve transmissions above 9...
متن کاملBottom Anti-Reflective Coatings (BARCs) for 157-nm!Lithography
Bottom anti-reflective coatings (BARCs) are essential for achieving the 65-nm node resolution target by minimizing the substrate reflectivity to less than 1% and by planarizing substrates. We believe that the developments in 157-nm BARC products are on track to make them available for timely application in 157-nm lithography. We have made some significant improvements in resist compatibility an...