Influence of N2 Partial Pressure on Structure and Mechanical Properties of TiAlN/Al2O3 Multilayers
نویسندگان
چکیده
TiAlN/Al2O3 multilayers with different Ar/N2 ratios were deposited on Si substrates in different N2 partial pressure by magnetron sputtering. The crystalline and multilayer structures of the multilayers were determined by a glancing angle X-ray diffractometer (XRD). A nanoindenter was used to evaluate the hardness, the elastic modulus and scratch scan of the multilayers. The chemical bonding was investigated by a X-ray Photoelectron Spectroscopy (XPS). The maximum hardness (36.3 GPa) and elastic modulus (466 GPa) of the multilayers was obtained when Ar/N2 ratio was 18:1. The TiAlN/Al2O3 multilayers were crystallized with orientation in the (111) and (311) crystallographic planes. The multilayers displayed stably plastic recovery in different Ar/N2 ratios. The scratch scan and post scan surface profiles of TiAlN/Al2O3 multilayers showed the highest critical fracture load (Lc) of 53 mN for the multilayer of Ar/N2 = 18:1. It indicated that the multilayer had better practical adhesion strength and fracture resistance.
منابع مشابه
Effect of N2 partial pressure on the structural and mechanical properties of TaN films
TaN films with different N2 partial pressure were deposited on 304 stainless steel using the magnetron sputtering method. The effect of gas pressure on the mechanical property, morphology and phase structure of the films is investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), microhardness testing, friction coefficient measurements, and wear mechanism study. The XRD results c...
متن کاملPhase Stability and Elasticity of TiAlN
We review results of recent combined theoretical and experimental studies of Ti1-xAlxN, an archetypical alloy system material for hard-coating applications. Theoretical simulations of lattice parameters, mixing enthalpies, and elastic properties are presented. Calculated phase diagrams at ambient pressure, as well as at pressure of 10 GPa, show a wide miscibility gap and broad region of composi...
متن کاملInfluence of Different Foaming Conditions on the Mechanical, Physical, and Structural Properties of Polypropylene Foam
In this article, the effects of different foam production times and temperatures on the mechanical, physical, and structural properties of polypropylene (PP) foam has been investigated. The microcellular PP foams were carried out using supercritical carbon dioxide (sc-CO2) as a physical foaming agent in a batch process. The samples were placed in a pressure vessel and were saturated ...
متن کاملKinetic comparison of Ni/Al2O3 and Ni/MgO-Al2O3 nano structure catalysts in CO2 reforming of methane
The kinetic characteristics of the Ni/Al2O3 and Ni/MgO-Al2O3 catalysts were investigated in CO2 reforming of methane (CRM). The reaction orders (α and β) and the rate constant (k) were calculated using the non-linear regression analysis, in which the sum of the squared differences of calculated and experimental CO2 reforming of m...
متن کاملEffect of increasing corundum on mechanical properties of silicon carbide refractories
Oxide materials such as Al2O corundum has a great influence on the mechanical and oxidation properties of refractory or refractory materials. In this paper, the effect of Al2O3 powder density, apparent porosity, linear shrinkage, and oxidation resistance of SiC composite refractory materials is investigated. Meanwhile, the compressive and flexural strengths were investigated before and after he...