Electroless Nickel Plating: Bath Control
نویسندگان
چکیده
In this paper, bath control is proposed for the electroless nickel plating through holes board process. The main parameters of the product (board) – thickness of the plating film and phosphorous content – are stabilized at constant levels using optimal tracking control. The set point for control is calculated from the model in dependence on the current state of the process. The pH-index and nickel percentage are stabilised at timevariable set points using simple feed-forward PI-control that is robust to the loading perturbation. Copyright © 2005 IFAC
منابع مشابه
Bath and Deposit Monitoring System for Electroless Nickel Plating Process
Electroless nickel plating is a widely used plating method in many industries. The usability of the coating is, however, restricted by the control problems related to the electroless nickel plating process. To ensure deposit quality, the transcendent properties of electroless nickel deposit should be accurately controlled during plating, which is challenging because of the spontaneous, unstable...
متن کاملCapillary Zone Electrophoresis for Electroless Plating Bath Samples
Capillary zone electrophoresis was used in the analysis of anions and cations in electroless plating bath samples. Examples described in this application note include the analysis of inorganic and organic anions in nickel-plating baths, cations in nickel-iron-cobalt-plating baths and metal-EDTA complexes in plating bath waste. Sample preparation was minimal, consisting merely of diluting the sa...
متن کاملElectroless Nickel Plating with Hypophosphite
In the previous chapter, the components of electroless nickel plating baths were discussed from the viewpoint of the function each performs in the bath, with little attention paid to their effect on the plating process. The metal and the electron source (the reducing agent) are consumed in the electroless plating reaction and so their concentrations in the bath are continuously decreasing. Ther...
متن کاملProlonging the Life of Electroless Nickel Plating Baths by Phosphite Removal
Electroless nickel plating baths have to be discarded when levels of phosphites build up and interfere with the plating process. OWMC funded research conducted at ORTECH International to determine whether phosphites could be removed from plating bath solution. The first attempt to do this by adsorption on flyash was unsuccessful. However, the use of calcium ion to precipitate calcium phosphite ...
متن کاملA Study on Electroless Deposition of Nickel on Nano Alumina Powder Under Different Sensitization Conditions
This paper deals with the preparation and characterization of Nickel-coated Alumina ceramic particles by Electroless Plating Technique. Nanosized α-Al2O3 powders of about 50nm in diameter are used for plating. The bath for Electroless Nickel Plating is prepared with NiCl2.6H2O, C6H5NaO7.H2O, NH4Cl and NaH2PO2.H2O. A bath temperature of 85°C, pH value of 8 and stirring time of 20 min is consider...