Fabrication of Carbonate Apatite Block through a Dissolution–Precipitation Reaction Using Calcium Hydrogen Phosphate Dihydrate Block as a Precursor
نویسندگان
چکیده
Carbonate apatite (CO₃Ap) block, which is a bone replacement used to repair defects, was fabricated through a dissolution-precipitation reaction using a calcium hydrogen phosphate dihydrate (DCPD) block as a precursor. When the DCPD block was immersed in NaHCO₃ or Na₂CO₃ solution at 80 °C, DCPD converted to CO₃Ap within 3 days. β-Tricalcium phosphate was formed as an intermediate phase, and it was completely converted to CO₃Ap within 2 weeks when the DCPD block was immersed in Na₂CO₃ solution. Although the crystal structures of the DCPD and CO₃Ap blocks were different, the macroscopic structure was maintained during the compositional transformation through the dissolution-precipitation reaction. CO₃Ap block fabricated in NaHCO₃ or Na₂CO₃ solution contained 12.9 and 15.8 wt % carbonate, respectively. The diametral tensile strength of the CO₃Ap block was 2 MPa, and the porosity was approximately 57% regardless of the carbonate solution. DCPD is a useful precursor for the fabrication of CO₃Ap block.
منابع مشابه
Bone Substitute Fabrication Based on Dissolution-Precipitation Reactions
Although blockor granular-type sintered hydroxyapatite are known to show excellent tissue responses and good osteoconductivity, apatite powder elicits inflammatory response. For the fabrication of hydroxyapatite block or granules, sintering is commonly employed. However, the inorganic component of bone and tooth is not high crystalline hydroxyapatite but low crystalline B-type carbonate apatite...
متن کاملFabrication of carbonate apatite block based on internal dissolution-precipitation reaction of dicalcium phosphate and calcium carbonate.
In this study, we investigated a novel method for fabrication of carbonate apatite block without ionic movement between precursor and solution by using precursor that includes all constituent ions of carbonate apatite. A powder mixture prepared from dicalcium phosphate anhydrous and calcite at appropriate Ca/P ratios (1.5, 1.67, and 1.8) was used as starting material. For preparation of specime...
متن کاملFabrication of solid and hollow carbonate apatite microspheres as bone substitutes using calcite microspheres as a precursor.
Spherical carbonate apatite (CO3Ap) microspheres approximately 1 mm in diameter were fabricated by granulation of calcium hydroxide around a core followed by carbonation and phosphatization through dissolution-precipitation reaction. CO3Ap microspheres with high uniformity could not be achieved without using a core. Solid CO3Ap microspheres were obtained using a calcite core whereas hollow CO3A...
متن کاملCalcium Acetate Versus Calcium Carbonate as Oral Phosphate Binder: Preparation and In Vitro Assessment
Calcium acetate is used as an oral phosphate binder to control hyperphosphatemia in patients with chronic renal failure. Compared to calcium carbonate, control of hyperphosphatemia can be achieved at lower calcium administration with calcium acetate which likely reduces the risk of hypercalcemia. In this study, various formulations of calcium acetate tablets were prepared and their disint...
متن کاملCALCIUM PHOSPHATE CEMENT: STUDY OF (BETA-TRICALCIUM PHOSPHATE, DICALCIUM PHOSPHATE AND CALCIUM CARBONATE SYSTEM
Calcium phosphate cements (CPCs), using B-tricalcium phosphate (ß-TCP, Ca3 (P04)2), dicalcium phosphate (DCP, CaHP04), calcium carbonate (Ca CO3), and hydroxylapatite (HAp, Ca10(P04)6(OH)2) as powder cement and disodium hydrogen phosphate (Na2HP04) solution as liquid component were prepared. After mixing the powder and liquid constituents, injectable and self-setting calcium phosphate cements (...