Structure of reverse microemulsion-templated metal hexacyanoferrate nanoparticles

نویسندگان

  • Alberto Gutiérrez-Becerra
  • Maximiliano Barcena-Soto
  • Víctor Soto
  • Jesús Arellano-Ceja
  • Norberto Casillas
  • Sylvain Prévost
  • Laurence Noirez
  • Michael Gradzielski
  • José I Escalante
چکیده

The droplet phase of a reverse microemulsion formed by the surfactant cetyltrimethylammonium ferrocyanide was used as a matrix to synthesize nanoparticles of nickel hexacyanoferrate by adding just a solution of NiCl2 to the microemulsion media. Dynamic light scattering and small-angle neutron scattering measurements show that the reverse microemulsion droplets employed have a globular structure, with sizes that depend on water content. Transmission electron microscopy and electron diffraction are used to obtain information about the structure of the synthesized nanoparticles. The results show that the size and shape of the coordination compound nanoparticles correspond with the size and shape of the droplets, suggesting that the presented system constitutes an alternative method of the synthesis of metal hexacyanoferrate nanoparticles.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Synthesis of Iron Yttrium Garnet Nanoparticles by Reverse Microemulsion Method

Colloidal nanodispersion of Iron Yttrium Garnet has been preparedbymixing the two ternary mixture of Triton X-100 (surfactant), n-heptane and aqueous solution that differing only in the aqueous phase.Ethanolwas added as cosurfactant and mixed them by ultrasound bath. By mixing these twomicroemulsions, Iron Yttrium garnet (Y3 Fe5 O12) nanodispersionwas obtained. Solids were settled by centrifuge...

متن کامل

Formation of Needle Like Hydroxyl Apatite by Polyelectrolyte-modified Inverse Microemulsion Technique

In this work needle like hydroxy apatite were synthesized in a reverse microemulsion droplets of water in cyclohexane, separated by a cationic surfactant and co-surfactant, in the presence of Na-polyacrylate (PAA) as an anionic polyelectrolyte. Characterization of the as formed HAp nanoparticles at the room temperature were carried out by X-ray diffraction (XRD) and Fourier transform infrared s...

متن کامل

Synthesis and Investigation the Catalytic Behavior of Cr2O3 Nanoparticles

The use of an inorganic phase in water-in-oil (w/o) microemulsion has recently received considerable attention for preparing metal oxide nanoparticles. This is a technique, which allows preparation of ultrafine metal oxide nanoparticles within the size range 40 to 80 nm. Preparation of nano chromium (III) oxide studied investigated in the inverse microemulsion system. Therefore the nucleation o...

متن کامل

Formation of Needle Like Hydroxyl Apatite by Polyelectrolyte-modified Inverse Microemulsion Technique

In this work needle like hydroxy apatite were synthesized in a reverse microemulsion droplets of water in cyclohexane, separated by a cationic surfactant and co-surfactant, in the presence of Na-polyacrylate (PAA) as an anionic polyelectrolyte. Characterization of the as formed HAp nanoparticles at the room temperature were carried out by X-ray diffraction (XRD) and Fourier transform infrared s...

متن کامل

Synthesis and Characterization of HighTemperature Stable Nanocomposite Catalysts

Unusually active and sinter-resistant nanocomposite materials were synthesized by combining the high reactivity of nanosized noble metal particles with the excellent hightemperature stability of hexa-aluminates through a simple one-step microemulsion-templated sol-gel synthesis. The novel nanocomposite catalysts were characterized by TEM, XRD, DTA and BET measurements after calcination at tempe...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 7  شماره 

صفحات  -

تاریخ انتشار 2012