Oxidation of FePt nanoparticles
نویسندگان
چکیده
Chemically disordered B3–7-nm-diameter FePt nanoparticles are synthesized using the airless operation technique based on decomposition of iron pentacarbonyl and reduction of platinum acetylacetonate. The particle solution is then washed and subsequently deposited onto a thermally oxidized Si substrate. Nanoparticle assemblies are formed after solvent evaporation. The samples are heat-treated using rapid thermal annealing at 650 C for 30min, in an atmosphere of Ar gas with less than 1 ppm of O2. Oxidation has to be avoided to obtain the FePt L10 phase. Other crystalline phases such as FePt3 (L12), magnetite Fe3O4, hematite Fe2O3 and FCC Pt are obtained if oxygen is present. r 2003 Elsevier B.V. All rights reserved.
منابع مشابه
Magnetic Properties of FePt Nanoparticles Prepared by a Micellar Method
FePt nanoparticles with average size of 9 nm were synthesized using a diblock polymer micellar method combined with plasma treatment. To prevent from oxidation under ambient conditions, immediately after plasma treatment, the FePt nanoparticle arrays were in situ transferred into the film-growth chamber where they were covered by an SiO2 overlayer. A nearly complete transformation of L10 FePt w...
متن کاملElectro-oxidation of formic acid catalyzed by FePt nanoparticles.
The electrocatalytic oxidation of formic acid at a gold electrode functionalized with FePt nanoparticles was studied by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) in a mixed solution of 0.1 M HCOOH and 0.1 M HClO4. The FePt bimetallic nanoparticles, with a mean diameter of 3 nm, were prepared by a chemical reduction method. The Au/FePt nanostructured electrode was ...
متن کاملElectro-oxidation of formic acid catalyzed by FePt nanoparticlesw
The electrocatalytic oxidation of formic acid at a gold electrode functionalized with FePt nanoparticles was studied by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) in a mixed solution of 0.1 M HCOOH and 0.1 M HClO4. The FePt bimetallic nanoparticles, with a mean diameter of 3 nm, were prepared by a chemical reduction method. The Au/FePt nanostructured electrode was ...
متن کاملRole of different platinum precursors on the formation and reaction mechanism of FePt nanoparticles and their electrocatalytic performance towards methanol oxidation.
We report the formation mechanism of FePt nanoparticles (NPs) by a high temperature polyol method using an equimolar ratio of Fe and Pt-precursor with different Pt-precursors. Pt(acac)2, PtCl2, PtCl4 and H2PtCl6·H2O were used as Pt-precursors and Fe(acac)3 as the only Fe-precursor. Different stoichiometric compositions along with variation in size were obtained by using different precursors of ...
متن کاملSynthesis and Morphology of Face Centered Cubic (FCC) Fe-Pt Nanoparticles
FePt nanoparticles with thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles are prepared by chemical synthesis and a salt-matrix annealing technique. Structural and magnetic characterizations confirm the phase transition from the disordered face-centered cubic structure. In this paper, 3 nm FePt nanoparticles are first synthesized by superhydride re...
متن کامل