The effect of three silane coupling agents and their blends with a cross-linker silane on bonding a bis-GMA resin to silicatized titanium (a novel silane system).

نویسندگان

  • J P Matinlinna
  • L V J Lassila
  • P K Vallittu
چکیده

OBJECTIVES Three activated organofunctional silane coupling agents alone and blended with a non-functional cross-linker silane were evaluated as adhesion promoters in an experiment where a bis-GMA (bis-phenol-A-diglycidyldimethacrylate) resin was bonded to silicatized titanium. The adhesive performances of the silanes were assessed as shear bond strength values. MATERIALS AND METHODS 3-Methacryloyloxypropyltrimethoxysilane, N-[3-(trimethoxysilyl)propyl]ethylenediamine and [3-(triethoxysilyl)propyl]urea were prepared as 1.0vol.% solutions in 95 vol.% ethanol. They were each also blended with 1.0 vol.% 1,2-bis-(triethoxysilyl)ethane solutions that were activated for 1 or 24 h. Titanium slides were cleaned, silicatized, distributed randomly to study groups and silanized with nine silane solutions. After silanization experimental bis-GMA resin stubs were photo-polymerized and post-polymerized in a light-curing unit. The shear bond strength was measured as 'dry samples' and after thermo-cycling (6000 cycles at 5-55 degrees C). RESULTS The type of silane affected significantly the shear bond strength (p<0.001) and the use of cross-linker silane (p<0.005) according to the statistical analysis (ANOVA). It showed that the highest shear bond strength for thermo-cycled resin stub samples (n=8/group) was obtained with a blend of 1.0vol.% 3-methacryloyloxypropyltrimethoxysilane+1.0 vol.% 1,2-bis-(triethoxysilyl)ethane blend (10.4+/-3.5 MPa). The lowest results were obtained with 1.0 vol.% [3-(triethoxysilyl)propyl]urea (4.5+/-1.0 MPa), and with 1.0 vol.% N-[3-(trimethoxysilyl)propyl]ethylenediamine (4.5+/-1.4 MPa). CONCLUSIONS Silanization with a blend of a functional silane and a cross-linker silane (a novel silane system) might improve the hydrolytic stability of a siloxane film between silicatized titanium and a bis-GMA resin.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Silane and bonding of Resins to Ceramic

Silane and bonding of Resins to Ceramic Dr. K. Seyyedan* - Dr. M. Kalalipoor** - Dr. M. Javan***Assistant Professor of Fixed Prosthodontics Dept., Faculty of Dentistry, Shaheed Beheshti University of Medical Sciences. **Resident of Fixed Prosthodontics Dept., Faculty of Dentistry, Shaheed Beheshti University of Medical Sciences. Background and Aim: When bonding between two different dental mate...

متن کامل

Shear bond strength between resin and zirconia with two different silane blends.

OBJECTIVE To study in vitro the effect of two cross-linking silanes, bis-1,2-(triethoxysilyl)ethane and bis[3-(trimethoxysilyl)propyl]amine, blended with an organofunctional silane coupling agent, (3-acryloxypropyl)trimethoxysilane, on the shear bond strength between resin-composite cement and silicatized zirconia after dry storage and thermocycling. MATERIALS AND METHODS Six tested groups of...

متن کامل

Title Enhanced resin-composite bonding to zirconia framework after pretreatment with selected silane monomers

Objective. To evaluate the effect of five experimental silane monomer primers in vitro on the shear bond strength of a phosphate ester resin-composite cement bonded to silicatized zirconia framework. Methods. A total of 144 planar zirconia (Procera AllZircon) specimens were subjected to tribochemical silica-treatment, randomly divided into 12 sub-groups (n=12), and silanized with 1.0% (v/v) act...

متن کامل

Nitroxide-Mediated Radical Polymerization of Styrene Initiated from the Surface of Titanium Oxide Nanoparticles

Titanium dioxide (TiO2) nanoparticles, with an average size of about 45 nm, were encapsulated by polystyrene using in situ nitroxide mediated radical polymerization   in the presence of 3-aminopropyl triethoxy silane (APTES) as a coupling agent and 2, 2, 6, 6-tetramethylpiperidinyl-1-oxy  as a initiator. First, the initiator for NMRP was covalently bonded onto the surface of Titanium dioxide na...

متن کامل

مقایسه اثر سه ماده اچ کننده پرسلن (PHA-APF-HF) بر روی استحکام برشی باند کامپوزیت- پرسلن

Statement of Problem: Porcelain restorations are susceptible to fracture and a common method for repairing is the use of silane and composite on etched porcelain. Although HF is very effective in porcelain etching but has detrimental effects on tissues. Purpose: In this study, the effect of APF and PHA was compared with HF in porcelain etching. Also the role of silane, unfilled resin and dentin...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Journal of dentistry

دوره 34 10  شماره 

صفحات  -

تاریخ انتشار 2006