The effect of margin thickness, degree of convergence and bonding interlayer on the marginal failure of glass-simulated all-ceramic crowns.
نویسندگان
چکیده
The objectives of this study were to identify the effect of design parameters, namely marginal thickness, degree of convergence and the different interfacial conditions, on the initial failure load that induces cracking from the margin in glass-simulated dental crowns. Crown-like glass cylinders were prepared to simulate posterior all-ceramic crowns with two different marginal thicknesses (0.8 or 1.2mm) and degrees of convergence (6° or 12°). A three-step bonding system was used complementarily with a silane coupling agent to adhesively bond the specimens to resin dies. The crowns were subjected to an axial applied load to generate hoop tensile stress at the crown margin. The entire loading and fracture processes were recorded by video camera. The loading data were compared with the other two interfacial treatments (Vaseline grease and directly poured uncured resin on glass). The Weibull distribution was used to statistically analyze the characteristic failure load and the mean values. The fracture surfaces were fractographically analyzed along with the load-displacement curves, and the degrees of crack stability for each parameter were also identified. It was found that there is no difference in the initial failure load between the different marginal thicknesses in all interfacial conditions. The bonded crowns present more resistance to crack propagation. The higher convergence crown preparation can reduce the initial failure load at the crowns' margin, which can be resisted by a strongly bonded interface. Clear interactions between margin design parameters and their effects on the stress development and crack propagation are necessary to develop an appropriate design of all-ceramic crowns.
منابع مشابه
The Effect of Different Finishing Lines on the Marginal Fitness of Full Contour Zirconia and Glass Ceramic CAD/CAM Crowns (An in-vitro study)
Purpose: The aim of this study was to evaluate the effect of two gingival finishing lines (90° shoulder and deep chamfer) on the marginal fitness of two types of full anatomic all-ceramic crowns; zirconia crowns (Zikonzhan) and glass ceramic crowns (IPS e-max CAD) milled with CAD/CAM system. Materials and Methods: Two dentoform teeth of left maxillary first molar were prepared with chamfer fini...
متن کاملEffect of Core Thickness and Porcelain Sintering on Marginal Adaptation
Background and aim: Marginal adaptation affects the long-term success of full-coverage restorations. This study aimed to assess the effect of porcelain sintering and zirconia core thickness on the marginal adaptation of all-ceramic restorations. Materials and methods: In this in-vitro experimental study, a standard brass die, 7 mm in length and 5 mm in diameter, was fabricated using a milling ...
متن کاملThe Effect of Different Marginal Designs on the Fracture Resistance of Monolithic Zirconia Crowns
Abstract Background and Aim: One of the major problems of all ceramic restorations is their probable fracture against the occlusal force. The aim of the present in vitro study is to compare the effect of three marginal designs (shoulder, sloped shoulder, chamfer) on the fracture resistance of monolithic zirconia crowns. Materials and methods: In this in vitro study, three PEEK dies with cham...
متن کاملThe Third International Conference on Computational Modeling of Fracture and Failure of Materials and Structures
In dentistry, many preparation guidelines for allceramic crowns are still based upon clinical experience and those developed for metal ceramic crowns that may not be applicable and need further experimental and numerical evaluation. Some specific features are requiring investigation in dental prosthetic devices, for example, configurations of the crowns’ margin [1], marginal thickness [2, 3] an...
متن کاملMarginal Assessment of Crowns by the Aid of Parallel Radiography
Introduction: Marginal adaptation is the most critical item in long-term prognosis of single crowns. This study aimed to assess the marginal quality as well asthe discrepancies in marginal integrity of some PFM single crowns of posterior teeth by employing parallel radiography in Shiraz Dental School, Shiraz, Iran. Methods: In this descriptive study, parallel radiographies were taken from 200 f...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Acta biomaterialia
دوره 8 12 شماره
صفحات -
تاریخ انتشار 2012