Hemispherical total emissivity and specific heat capacity of deeply undercooled Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 melts
نویسندگان
چکیده
High-temperature high-vacuum electrostatic levitation ~HTHVESL! and differential scanning calorimetry ~DSC! were combined to determine the hemispherical total emissivity eT , and the specific heat capacity cp , of the undercooled liquid and throughout the glass transition of the Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 bulk metallic glass forming alloy. The ratio of cp /eT as a function of undercooling was determining from radiative cooling curves measured in the HTHVESL. Using specific heat capacity data obtained by DSC investigations close to the glass transition and above the melting point, eT and cp were separated and the specific heat capacity of the whole undercooled liquid region was determined. Furthermore, the hemispherical total emissivity of the liquid was found to be about 0.22 at 980 K. On undercooling the liquid, the emissivity decreases to approximately 0.18 at about 670 K, where the undercooled liquid starts to freeze to a glass. No significant changes of the emissivity are observed as the alloy undergoes the glass transition. © 1995 American Institute of Physics.
منابع مشابه
A Method Based on Radiative Cooling for Detecting Changes in Undercooked Metallic Liquids
We introduce a structure-sensitive parameter for unclercooled melts which can be measured in containerless We have established that the ratio, R(T), emissivity eT(T) to constant-pressure specific processing experiments. of hemispherical total heat CP(T) can serve as an indicator which is sensitive to any changes in short range atomic order in undercooked metallic melts. R(T) = E~(T)/c P(T) valu...
متن کاملDecomposition and primary crystallization in undercooled Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 melts
Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 bulk metallic glasses were prepared by cooling the melt with a rate of about 10 K/s and investigated with respect to their chemical and structural homogeneity by atom probe field ion microscopy and transmission electron microscopy. The measurements on these slowly cooled samples reveal that the alloy exhibits phase separation in the undercooled liquid state. Signi...
متن کاملMeasurements of Specific Heat Capacity and Hemispherical Total Emissivity at High Temperatures Using a Feedback- Controlled Pulse-heating Technique
متن کامل
Thermodynamics and kinetics of the undercooled liquid and the glass transition of the Zr41.2Ti13.8Cu12.5Ni10.0Be22.5 alloy
Differential scanning calorimetry (DSC) was used to determine the thermodynamic functions of the undercooled liquid and the amorphous phase with respect to the crystalline state of the ~41.2Ti13.8CU125Nilo.OBe22.5 bulk mltallic glass forming alloy. The specific heat capacities of this alloy. in the undercooled liquid, the amorphous state and the crystal were determined. The differences in entha...
متن کاملThe Origins of Spontaneous Grain Refinement in Deeply Undercooled Metallic Melts
Phase-field modeling of rapid alloy solidification, in which the rejection of latent heat from the growing solid cannot be ignored, has lagged significantly behind the modeling of conventional casting practices which can be approximated as isothermal. This is in large part due to the fact that if realistic materials properties are adopted, the ratio of the thermal to solute diffusivity (the Lew...
متن کامل