Fabrication of CuO nanoparticle interlinked microsphere cages by solution method
نویسندگان
چکیده
Here we report a very simple method to convert conventional CuO powders to nanoparticle interlinked microsphere cages by solution method. CuO is dissolved into aqueous ammonia, and the solution is diluted by alcohol and dip coating onto a glass substrate. Drying at 80 C, the nanostructures with bunchy nanoparticles of Cu(OH)2 can be formed. After the substrate immerges into the solution and we vaporize the solution, hollow microspheres can be formed onto the substrate. There are three phases in the as-prepared samples, monoclinic tenorite CuO, orthorhombic Cu(OH)2, and monoclinic carbonatodiamminecopper(II) (Cu(NH3)2CO3). After annealing at 150 C, the products convert to CuO completely. At annealing temperature above 350 C, the hollow microspheres became nanoparticle interlinked cages.
منابع مشابه
Fabrication of high–strength alumina composite foams through gel–casting process
A water–soluble gelatin combined with polyethylene microspheres were developed to prepare alumina composite foam. Gelatin was used as the gelling agent and polyethylene was used as pore making template. On the other hand, kaolin was used to provide green strength and CuO was applied to decrease the required temperature as a sinter aid. Alumina bodies need elevate temperature for sintering, incr...
متن کاملEffect of temperature and time on morphology of CuO nanoparticle during synthesis
In the past decades, many methods have been developed to synthesize zero- dimensional nanoparticles, quasi–one–dimensional (1D) CuO nanostructures, such as metal organic deposition technique, microwave irradiation, sol-gel-like dip technique, reverse micelle-assisted route, chemical method, and simple template free solution route. Among those synthesis methods, hydrothermal and chemical reac...
متن کاملEffect of temperature and time on morphology of CuO nanoparticle during synthesis
In the past decades, many methods have been developed to synthesize zero- dimensional nanoparticles, quasi–one–dimensional (1D) CuO nanostructures, such as metal organic deposition technique, microwave irradiation, sol-gel-like dip technique, reverse micelle-assisted route, chemical method, and simple template free solution route. Among those synthesis methods, hydrothermal and chemical reac...
متن کاملElectrochemical Detection of Hydrazine Using a Copper oxide Nanoparticle Modified Glassy Carbon Electrode
Metallic copper nanoparticles modified glassy carbon electrode is fabricated by reduction of CuSO4 in the presence of cetyltrimethylammonium bromide (CTAB) through potentiostatic method. As-prepared nanoparticles are characterized by scanning electron microscopy and electrochemical methods. Copper oxide modified glassy carbon electrode (nano-CuO/MGCE) is prepared using consecutive potential sca...
متن کاملSize ratio effects on interparticle interactions and phase behavior of microsphere-nanoparticle mixtures.
We investigate the interparticle interactions and phase behavior of microsphere-nanoparticle mixtures of high charge asymmetry and varying size ratio. In the absence of nanoparticles, negligibly charged microspheres flocculate as a result of van der Waals interactions. Upon addition of a lower critical nanoparticle volume fraction, the microspheres are stabilized by the formation of nanoparticl...
متن کامل