Influence of Phosphorus Micro-Segregation on Ferrite Structure in Cast Strips of 0.1mass% C Steel
نویسندگان
چکیده
Cast strips of 0.1mass% C steel with or without phosphorus addition have been characterized by electron back-scattering diffraction pattern (EBSP) measurements. Then the formation of globular ferrite structure was discussed. EBSP analysis combined with optical microscopy clearly showed that a globular grain was fitted to be an -ferrite grain. The EBSP analysis suggested that the retainedgrain grew predominantly in the -grain and formed the globular -ferrite during cooling. The microtexture in the globular ferrite structure depended highly on the solidification structure. It is important to scatter the primary dendrite growth direction into neighboring areas to develop fine priorand structures for the cast strip of high-phosphorus steel.
منابع مشابه
Influence of Cu and Ni on the Microstructure and Mechanical Properties of an HSLA Steel
In this research the role of alloying elements on the microstructure and mechanical properties of an as cast and hot rolled high strength low alloy (HSLA) steel was studied. Different compositions with different amount of copper in the presence of nickel, hot rolled and quenched in oil. Tensile test, hardness test, scanning electron microscope (SEM) and optical microscope (OM) were used to eval...
متن کاملThe Influence of Homogenization and Solution Annealing Process on the Microstructure and Mechanical Properties of 1.4470 Ferritic-austenitic Stainless Steel
In the present research, the effect of the homogenization process and annealing temperature were investigated for the 1.4470 ferritic-austenitic stainless steel in the as-cast condition. In this regard, microstructural evolutions, hardness, and impact energy of the steel was evaluated with different heat treatment conditions. The results show that the minimum volume fraction of austenite phase ...
متن کاملOn Microstructure Development and Inclusion Generation in a Continuously Cast Resulphurised Steel
−− An experimental study on solidification structure development and on endogenous inclusion precipitation in a continuously cast resulphurised steel is presented. Results were obtained by investigating two heats of a free cutting C-Mn steel cast in billets with a diameter of 145 mm. The as cast structure was evaluated by macroand microscopic analyses. Primary and secondary dendrite arm spacing...
متن کاملEffect of Thermomechanical Processing on the Microstructure and Mechanical Properties of a Duplex Stainless Steel
Duplex stainless steels (DSSS) have a microstructure composed of ferrite and austenite phases that gives them a very good combination of mechanical and corrosion properties. These steels are desirable for many applications in the chemical and petrochemical industries. In the present study, a type of stainless steel was cast, solution annealed at 1200°C for 60 min and then quenched in water. Ini...
متن کاملEffects of Homogenization Conditions and Hot Rolling Parameters on Grain Refinement of an As-Cast 301 Stainless Steel
In this work, effects of homogenization time of 3 to 13 h at 1200 °C on the grain refinement of as-cast AISI 301 stainless steel after different hot rolling conditions were investigated. The results showed that the minimum grain size of 16±7 mm was achieved when homogenization took place at 1200 °C for 9 h followed by hot rolling at temperature range of 1000–1200 °C with strain of 0.8 and stra...