Controllable synthesis of branched ZnO/Si nanowire arrays with hierarchical structure
نویسندگان
چکیده
A rational approach for creating branched ZnO/Si nanowire arrays with hierarchical structure was developed based on a combination of three simple and cost-effective synthesis pathways. The crucial procedure included growth of crystalline Si nanowire arrays as backbones by chemical etching of Si substrates, deposition of ZnO thin film as a seed layer by magnetron sputtering, and fabrication of ZnO nanowire arrays as branches by hydrothermal growth. The successful synthesis of ZnO/Si heterogeneous nanostructures was confirmed by morphologic, structural, and optical characterizations. The roles of key experimental parameters, such as the etchant solution, the substrate direction, and the seed layer on the hierarchical nanostructure formation, were systematically investigated. It was demonstrated that an etchant solution with an appropriate redox potential of the oxidant was crucial for a moderate etching speed to achieve a well-aligned Si nanowire array with solid and round surface. Meanwhile, the presence of gravity gradient was a key issue for the growth of branched ZnO nanowire arrays. The substrate should be placed vertically or facedown in contrast to the solution surface during the hydrothermal growth. Otherwise, only the condensation of the ZnO nanoparticles took place in a form of film on the substrate surface. The seed layer played another important role in the growth of ZnO nanowire arrays, as it provided nucleation sites and determined the growing direction and density of the nanowire arrays for reducing the thermodynamic barrier. The results of this study might provide insight on the synthesis of hierarchical three-dimensional nanostructure materials and offer an approach for the development of complex devices and advanced applications.
منابع مشابه
Synthesis of ZnO/Si Hierarchical Nanowire Arrays for Photocatalyst Application
ZnO/Si nanowire arrays with hierarchical architecture were synthesized by solution method with ZnO seed layer grown by atomic layer deposition and magnetron sputtering, respectively. The photocatalytic activity of the as-grown tree-like arrays was evaluated by the degradation of methylene blue under ultraviolet light at ambient temperature. The comparison of morphology, crystal structure, optic...
متن کاملTailoring n-ZnO/p-Si branched nanowire heterostructures for selective photoelectrochemical water oxidation or reduction.
We report the fabrication of three-dimensional (3D) branched nanowire (NW) heterostructures, consisting of periodically ordered vertical Si NW trunks and ZnO NW branches, and their application for solar water splitting. The branched NW photoelectrodes show orders of magnitudes higher photocurrent compared to the bare Si NW electrodes. More interestingly, selective photoelectrochemical cathodic ...
متن کاملSynthesis, characterization and electrical properties of hybrid Zn2GeO4–ZnO beaded nanowire arrays
We report the syntheses of vertically aligned, beaded zinc germinate (Zn2GeO4)/zinc oxide (ZnO) hybrid nanowire arrays via a catalyst-free approach. Vertically aligned ZnO nanowire is used as a lattice matching reactive template for the growth of Zn2GeO4/ZnO nanowire. The morphology and structure of the as-prepared samples were characterized using X-ray diffractometry (XRD), scanning electron (...
متن کاملGrowth and replication of ordered ZnO nanowire arrays on general flexible substrates
Vertically aligned and site controllable ZnO nanowire arrays have been synthesized and replicated via hydrothermal method on general flexible substrates. The replication was demonstrated for three generations. The morphology and density of the nanowire arrays could be optimized in the original generation by adjusting the chemical reaction parameters. The pattern of the original generation was i...
متن کاملGrowth of ZnO nanowires on retroreflector microspheres and the resulting light channeling and plasmonic properties
We have investigated the growth of ZnO nanowires on curved BaTi03 retroreflector beads, as well as grov.1h of ZnO nanowires on flat substrates. Results indicate that the growth of ZnO aligned nanowire arrays occurs farther away from the Zn source in the retroreflectors, while the results are opposite for the flat Si substrates. In the case of the ZnO nanowires on flat Si, the nanowires formed i...
متن کامل