A simple combinatorial method to discover Co-Mo binary catalysts that grow vertically aligned single-walled carbon nanotubes

نویسندگان

  • Suguru Noda
  • Hisashi Sugime
  • Toshio Osawa
  • Yoshiko Tsuji
  • Shohei Chiashi
  • Yoichi Murakami
  • Shigeo Maruyama
چکیده

A simple yet versatile combinatorial method to discover binary metal nanoparticle catalysts was developed. In this method, the nominal thickness of component metals can be independently screened for a wide range by simply setting a mask with a slit above a substrate during sputter-deposition. Using this method, we prepared a catalyst library with Mo (0.2− 4 nm) and Co (0.2− 8 nm) thickness profiles on a SiO2/Si wafer and discovered active catalysts that grow vertically aligned single-walled carbon nanotubes by alcohol catalytic chemical vapor deposition.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Controlling the growth of vertically oriented single-walled carbon nanotubes by varying the density of CoAMo catalyst particles

A simple method to grow vertically aligned arrays of various forms of single-walled carbon nanotubes (V-SWNT) is reported. CO disproportionation on CoAMo bimetallic catalysts has been used in the synthesis. Resonant Raman and transmission electron microscope (TEM) were employed to characterize the as-produced SWNTs, which display a high purity and very low concentration of other carbon forms. C...

متن کامل

Multiple “optimum” conditions for Co-Mo catalyzed growth of vertically aligned single-walled carbon nanotube forests

Carbon nanotubes (CNTs) were grown directly on substrates by alcohol catalytic chemical vapor deposition using a Co-Mo binary catalyst. Optimum catalytic and reaction conditions were investigated using a combinatorial catalyst library. High catalytic activity areas on the substrate were identified by mapping the CNT yield against the orthogonal gradient thickness profiles of Co and Mo. The loca...

متن کامل

Diameter and morphology control of SWNTs by alcohol CVD

The concentration of Co-Mo binary catalyst concentration and the effect on the morphology of single-walled carbon nanotubes (SWNT) was investigated by scanning electron microscopy and optical spectroscopy. We found that there is some critical concentration or catalyst density below which SWNTs will not be vertically aligned. Higher Mo concentrations resulted in vertically aligned, small-diamete...

متن کامل

Morphology and chemical state of Co-Mo catalysts for growth of single-walled carbon nanotubes vertically aligned on quartz substrates

Bimetallic catalysts (Co:Mo ≈ 2:1 in atomic ratio) were prepared on quartz substrates from metal acetate solutions using a procedure of dip coating, followed by calcination and reduction. High-purity single-walled carbon nanotubes (SWNTs) 1–2 nm in diameter were grown densely (~1.0×10 17 m-2) and vertically on these substrates during an alcohol catalytic chemical vapor deposition process. To cl...

متن کامل

Reduction of single-walled carbon nanotube diameter to sub-nm via feedstock

Vertically aligned single-walled carbon nanotube arrays were synthesized from dip-coated binary Co/Mo catalyst by no-flow chemical vapor deposition from either pure ethanol or acetonitrile as carbon feedstock. By changing to acetonitrile the mean diameter was reduced from 2.1 nm to less than 1.0 nm despite using identically prepared catalyst. The demonstrated diameter control on flat substrates...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2007