Optical properties of Ni and Cu nanowire arrays and Ni/Cu superlattice nanowire arrays
نویسندگان
چکیده
: In this study, Ni and Cu nanowire arrays and Ni/Cu superlattice nanowire arrays are fabricated using standard techniques such as electrochemical deposition of metals into porous anodic alumina oxide templates having pore diameters of about 50 nm. We perform optical measurements on these nanowire array structures. Optical reflectance (OR) of the as-prepared samples is recorded using an imaging spectrometer in the wavelength range from 400 to 2,000 nm (i.e., from visible to near-infrared bandwidth). The measurements are carried out at temperatures set to be 4.2, 70, 150, and 200 K and at room temperature. We find that the intensity of the OR spectrum for nanowire arrays depends strongly on the temperature. The strongest OR can be observed at about T = 200 K for all samples in visible regime. The OR spectra for these samples show different features in the visible and near-infrared bandwidths. We discuss the physical mechanisms responsible for these interesting experimental findings. This study is relevant to the application of metal nanowire arrays as optical and optoelectronic devices.
منابع مشابه
Ternary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy.
 We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relatio...
متن کاملTernary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy. We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relation ...
متن کاملLarge-scale Ni-doped ZnO nanowire arrays and electrical and optical properties.
Large-scale Ni-doped ZnO nanowire (NW) arrays are grown. The electrical conductivity of a single Ni-doped ZnO NW has been increased for 30 times. The photoluminescence (PL) spectrum of the doped ZnO NWs has a red shift, suggesting possible doping induced band edge bending. The doped NW arrays could be the basis for building integrated nanoscale transistors, sensors, and photodetectors.
متن کاملSelective electrochemical reduction of CO2 to CO on CuO-derived Cu nanowires.
In this work, we report a new synthesis method to prepare a Cu nanowire electrocatalyst for selective CO2 reduction at room temperature and atmospheric pressure. Cu nanowire array electrodes were prepared through a two-step synthesis of Cu(OH)2 and CuO nanowire arrays on Cu foil substrates and a subsequent electrochemical reduction of the CuO nanowire arrays. The Cu nanowire arrays are able to ...