Recent Progress and Required Developments in Atmospheric Corrosion of Galvanised Steel and Zinc

نویسنده

  • Ivan S. Cole
چکیده

This paper reviews the progress in atmospheric corrosion of zinc since 2009. It firstly summarises the state of the art in 2009, then outlines progress since 2009, and then looks at the significance of this progress and the areas the need more research. Within this framework, it looks at climate effects, oxide formation, oxide properties, pitting, laboratory duplication of atmospheric corrosion, and modelling. The major findings are that there have been major advances in the fields understanding of the structure of corrosion patina, in particular their layered structure and the presence of compact layers, local corrosion attacks have been found to be a significant process in atmospheric corrosion and experiments under droplets are leading to new understanding of the criticality of drop size in regulating atmospheric corrosion processes. Further research is indicating that zinc oxide within corrosion products may promote the oxygen reduction reaction (ORR) and that, in porous oxides, the ORR would control pore chemistry and may promote oxide densification. There is a strong need for more research to understand more deeply the formation and properties of these layered oxides as well as additional research to refine and quantify our emerging understanding of corrosion under droplets.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

A comparison study on corrosion behavior of zinc phosphate and potassium zinc phosphate anticorrosive pigments

In this article, the effect of potassium on structure and anticorrosion properties of zinc phosphate pigments has been investigated. The co-precipitation method was selected as synthesis method of potassium zinc phosphate pigment. Then the synthesized pigment was characterized by x-ray diffraction XRD, Fourier transform infrared FTIR and Raman spectroscopy. Morphology of the powders was investi...

متن کامل

Anticorrosive Performance of Polyester–melamine Coating Fortified with Zinc Ferrite Nanoparticles

In this study, nanoparticle zinc ferrites with different particle sizes were synthesized via sol-gel method using ferric nitrate and zinc nitrate. The obtained gel was dried and calcined at three different temperatures (i.e. 500, 600 and 800 °C) for 2 h. Adequate amounts of the as-synthesized nanoparticle samples were then added to the mixture of polyester resin and formaldehyde resin. The ...

متن کامل

Acetylacetonate Complexes as New Corrosion Inhibitors in Phosphoric Acid Media: Inhibition and Synergism Study

The corrosion inhibition performance of acetylacetonate complexes of zinc(II), manganese(II), cobalt(II) and copper(II) on the mild steel substrate in 1M H3PO4 was studied using DC polarization. It was seen that the mentioned complexes decreased corrosion rate of mild steel in phosphoric acid media due to the adsorption on metal surface. The potential of mild steel shifted toward more active po...

متن کامل

Electrochemical Impedance Response of Zn and Galvanized Steel Corroding under Marine Atmospheric Environments

Impedance response of zinc and galvanized steel samples exposed in wet-dry cyclic condition using 0.05 M NaCl solution has been analyzed in order to evaluate their corrosion behavior. The wet-dry cyclic test was performed by exposing sample to alternate conditions of 1 h immersion in 0.05 M NaCl solution and 7 h drying at 298 K with relative humidity (RH) of 60% for 10 days consisting of 30 cyc...

متن کامل

CORROSION BEHAVIOR OF ZINC COATED STEEL REBAR IN HIGH-STRENGTH REINFORCED CONCRETE

A large number of reinforced concrete structures subjected to chloride ions. Two basicapproaches for preventing corrosion of reinforcing steel embedded in concrete are: Increasing theconsolidation of concrete and using different coating on rebars. In present research steel rebarsare coated in different ways: a) 40 µm of zinc electroplated on steel rebar b) Zinc powder withepoxy paste (zinc rich...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 10  شماره 

صفحات  -

تاریخ انتشار 2017