Effectiveness of Conformal Coat to Prevent Corrosion of Nickel-palladium-gold-finished Terminals

نویسنده

  • Michael Osterman
چکیده

Nickel-palladium-gold-finished terminals are susceptible to creep corrosion. Excessive creep corrosion can result in device failure due to insulation resistance loss between adjacent terminals. The mixed flowing gas test has been demonstrated to produce creep corrosion on parts with nickel-palladium-gold finished terminals. Conformal coats are often used to protect printed wiring assemblies from failure due to moisture and corrosion. However, coating may not be sufficient to protect lead terminations from failure. In this study, acrylic, silicone, urethane, parylene, and atomic layer deposit (ALD) coatings were examined for their effectiveness at preventing corrosion of nickel-palladium-gold-finished terminals. The coverage of each coating was examined, and assemblies were subjected to eight hours of mixed flowing gas as well as temperature cycling. Non-uniform coating thickness was observed in the areas of the terminals. On some areas, little to no coating material was found for the acrylic, silicone, and urethane coatings. Parylene, which had the most uniform coating, was found to provide the best resistance to corrosion, while corrosion products were observed on the terminals of inspected parts protected by the other coatings.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Galvanic Corrosion Behavior of Dental Alloys

There is a wide variety of dental alloys, ranging from nearly pure gold and conventional gold-based alloys to alloys based on silver, palladium, nickel, cobalt, iron, titanium, tin, and other metals (Table 1). The types of dental alloys have increased significantly since 1980s in order to change the market price of gold and palladium. Although gold alloys are the mate‐ rials of choice in this a...

متن کامل

Electrochemical Behaviour and Galvanic Effects of Titanium Implants Coupled to Metallic Suprastructures in Artificial Saliva

The aim of the present study is to analyze the electrochemical behavior of five different dental alloys: two cobalt-chromium alloys (CoCr and CoCr-c), one nickel-chromium-titanium alloy (NiCrTi), one gold-palladium alloy (Au), and one titanium alloy (Ti6Al4V), and the galvanic effect when they are coupled to titanium implants (TiG2). It was carried out by electrochemical techniques (open circui...

متن کامل

Effect of ENEPIG Surface Finish on the Vibration Reliability of Solder Interconnects

Surface finishes are used to preserve and promote solderability of exposed copper metallization on printed wiring boards. While in the best of worlds, the solder used in assembly should dictate the solder interconnect reliability, surface finishes are known to have an effect. The effect of surface finishes on solder interconnect reliability can be particularly strong under high strain rate load...

متن کامل

In vitro element release and biological aspects of base–metal alloys for metal-ceramic applications

Objective: The aims of this study were to investigate the release of element from, and the biological response in vitro to, cobalt-chromium alloys and other base-metal alloys used for the fabrication of metal-ceramic restorations. Material and methods: Eighteen different alloys were investigated. Nine cobalt-chromium alloys, three nickel-chromium alloys, two cobalt-chromium-iron alloys, one pal...

متن کامل

The Benefits of Enepig with Pure Pd for Gold Wire Bonding

As a surface finish, electroless nickel / electroless palladium / immersion gold (ENEPIG) has received increased attention for both packaging/IC-substrate and PWB applications. With a lower gold thickness compared to conventional electroless nickel / immersion gold (ENIG) the ENEPIG finish offers the potential for higher reliability, better performance and reduced cost.[1,2] This paper shows th...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2014