Microcellular foams made from gliadin

نویسندگان

  • S. Quester
  • M. Dahesh
  • R. Strey
چکیده

We have generated closed-cell microcellular foams from gliadin, an abundantly available wheat storage protein. The extraction procedure of gliadin from wheat gluten, which involves only the natural solvents water and ethanol, respectively, is described with emphasis on the precipitation step of gliadin which results in a fine dispersion of mostly spherical, submicron gliadin particles composed of myriad of protein molecules. A dense packing of these particles was hydrated and subjected to an atmosphere of carbon dioxide or nitrogen in a high-pressure cell at 250 bar. Subsequent heating to temperatures close to but still below 100 °C followed by sudden expansion and simultaneous cooling resulted in closed-cell microcellular foam. The spherical gliadin templates along with the resulting foam have been analyzed by scanning electron microscope (SEM) pictures. The size distribution of the primary particles shows diameters peaked around 0.54 μm, and the final foam cell size peaks around 1.2 μm, at a porosity of about 80 %. These are the smallest foam cell sizes ever reported for gliadin. Interestingly, the cell walls of these microcellular foams are remarkably thin with thicknesses in the lower nanometer range, thus nourishing the hope to be able to reach gliadin nanofoam.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Preparation of PMMA/MWNTs Nanocomposite Microcellular Foams by In-situ Generation of Supercritical Carbon Dioxide

Nanocomposites containing poly(methyl methacrylate) (PMMA) and surface functionalized Multi-Walled Carbon Nanotubes (MWNTs) were synthesized. The dispersion of MWNTs in PMMA was characterized using Transmission Electron Microscopy (TEM).The synthesized nanocomposites were successfully foamed using a simple method based on the in-situ generation of supercritical carbon dioxide (CO2</sub...

متن کامل

The linear elastic properties of microcellular foams

The mechanical behaviour of a new type of open-cell foam made by a thermally induced phase separation (TIPS) process was investigated. Foams made by the TIPS process are characterized by cell sizes which are 10-100 times smaller than conventional foam materials. In this work, the linear elastic modulus of these foams in dynamic tension/compression was measured. A comparison was made with the th...

متن کامل

تأثیر نانولوله‌های کربنی بر مورفولوژی سلولی فوم‌های نانوکامپوزیتی میکروسلولار PC/EPDM

This research aimed at producing microcellular foams (with cell size of 1-10 μm and cell density above 10 9 cell/cm3) from PC/EPDM in order to use in medical devices. Due to the weak nucleation behavior of microcellular polycarbonate foams, it is difficult to prepare them. This research provides valuable information regarding the possibility of making microcellular foams from this polymer by u...

متن کامل

Tensile and Morphological Properties of Microcellular Polymeric Nanocomposite Foams Reinforced with Multi-walled Carbon Nanotubes

Polyamide 6 (PA6) is used in many applications due to its advantages and improving its properties seems essential. For this purpose in the present study, PA6 was melt compounded with various multi-walled carbon nanotubes (MWCNTs) contents and then was foamed using Azodi carbon amide (ACA) as blowing agent under different injection molding conditions. Morphological properties were investigated u...

متن کامل

Impact Strength of High Density Solid-State Microcellular Polycarbonate Foams

The effect of density (relative densities 0.33 to 0.90) on the impact behavior of microcellular polycarbonate (PC) was investigated. Cell size and foaming gas content were also considered. Flexed-beam Izod impact tests were conducted and the impact strength of these foams appears to be a strong function of both density and cell size. The impact strength was observed to improve over the unproces...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 292  شماره 

صفحات  -

تاریخ انتشار 2014