Halloysite nanotube-based electrospun ceramic nanofibre mat: a novel support for zeolite membranes
نویسندگان
چکیده
Some key parameters of supports such as porosity, pore shape and size are of great importance for fabrication and performance of zeolite membranes. In this study, we fabricated millimetre-thick, self-standing electrospun ceramic nanofibre mats and employed them as a novel support for zeolite membranes. The nanofibre mats were prepared by electrospinning a halloysite nanotubes/polyvinyl pyrrolidone composite followed by a programmed sintering process. The interwoven nanofibre mats possess up to 80% porosity, narrow pore size distribution, low pore tortuosity and highly interconnected pore structure. Compared with the commercial α-Al2O3 supports prepared by powder compaction and sintering, the halloysite nanotube-based mats (HNMs) show higher flux, better adsorption of zeolite seeds, adhesion of zeolite membranes and lower Al leaching. Four types of zeolite membranes supported on HNMs have been successfully synthesized with either in situ crystallization or a secondary growth method, demonstrating good universality of HNMs for supporting zeolite membranes.
منابع مشابه
Polypyrrole-Coated Electrospun Nanofibre Membranes for Recovery of Au(III) from Aqueous Solution
In this paper, for the first time, polypyrrole-coated electrospun nanofibre mats have been used as separation membranes to electrolessly recover Au from aqueous [Au(III)Cl4] solutions, based on a continuous-flow membrane separation process. With a [Au(III)Cl4] solution passing through the nanofibre membrane, the Au(III) ions were converted into elemental Au. The gold recovered was deposited on ...
متن کاملDecolorization of Dyeing Effl uent by Novel Ultrafi ltration Ceramic Membrane from Low Cost Natural Material
This paper is devoted to the application of new low cost ceramic ultrafi ltration membranes material coming from the Tunisian ores (mud) which is usually considered as disastrous for the environment. A ceramic tubular support previously elaborated from mud was coated in the lumen side by slip casting method. After sintering at 650°C, the coated membrane shows homogeneou...
متن کاملA novel fabrication of PVA/Alginate-Bioglass electrospun for biomedical engineering application
Objecttive (s): Polyvinylalcohol (PVA) is among the most natural polymers which have interesting properties such as nontoxic nature, biodegradability and high resistance to bacterial attacks making it applicable for tissue scaffolds, protective clothing, and wound healing.Materials and Methods: In the current work, PVA and Na-Alginate nanocomposite scaffolds were prepared using the electrospinn...
متن کاملGenipin cross-linked electrospun chitosan-based nanofibrous mat as tissue engineering scaffold
Objective(s): To improve water stability of electrospun chitosan/ Polyethylene oxide (PEO) nanofibers, genipin, a biocompatible and nontoxic agent, was used to crosslink chitosan based nanofibers. Materials and Methods: Different amounts of genipin were added to the chitosan/PEO solutions, chitosan/PEO weight ratio 90/10 in 80 % acetic acid, and the solutions were then electrospun to form nano...
متن کاملSynthesis and Characterization of a Novel Modified ANA Zeolite Membrane
A Novel modified Analcime (Na16 (Al16Si32O96) •16H2O) zeolite with a new molar ratio have been successfully synthesized. In order to investigate the role of the template, Different samples were synthesized with and without Tetramethylammoniumhydroxide (TMAOH) template through hydrothermal method. Different synthesis times (24, 36 and 72 hours) and molar ratios have been utilized. The optimum sa...