Influence of light-curing distance on degree of conversion and cytotoxicity of etch-and-rinse and self-etch adhesives

BACKGROUND The degree of conversion (DC) of resin based materials depends, beside other factors, on the light-intensity applied during light curing. A lower DC might be correlated with an increased cytotoxicity of the respective materials. Therefore, aim of the present study was to investigate the influence of the distance between light-curing tip and adhesives on their cytotoxicity and degree of conversion (DC). METHODS For the cytotoxicity assay, a total of 98 bovine dentine samples were prepared, distributed to seven groups (G1-G7; n = 14) and treated as follows: G1: untreated; G2-G4: OptiBond FL; G5-G7: OptiBond All-In-One. Adhesives were light-cured (1200 mW/cm(2)) at 1 mm (G2;G5), 4 mm (G3;G6) or 7 mm (G4;G7) distance. Samples were stored in culture media for 24 h and extracts were added to cell cultures (dental pulp cells and gingival fibroblasts) for a further 24 h. Finally, released lactate dehydrogenase activity (LDH) was photometrically determined, as measure for the cytotoxic effects of the extracts. The cytotoxicity assay was performed three times. Additionally, the DC of the adhesives was determined by FTIR spectroscopy. DC measurements were performed five times. RESULTS For both cell types, no significant difference of LDH release was observed between untreated control group (G1) and treated groups G2-G7 (p > 0.05, respectively), between the groups treated with same adhesive and light-cured at different distance (p > 0.05, respectively), as well as between groups treated with different adhesives and light-cured at the same distance (p > 0.05, respectively). Within the respective adhesive, no significant difference in the DC was observed when light-cured at different distance (p > 0.05, respectively), while OptiBond FL showed significantly higher DCs compared to OptiBond All-In-One when light-cured at same distances (p < 0.05, respectively). CONCLUSIONS The distance between light-curing tip and adhesive surface does not significantly influence either the cytotoxicity or the DC of the tested adhesives.