Electrochemical Formation of Multilayer SnO2-Sb xOy Coating in Complex Electrolyte
نویسندگان
چکیده
The multilayer antimony-doped tin dioxide coating was obtained by cathodic deposition of multilayer metal-hydroxide coating with near 100-nm thickness layers on the alloy underlayer accompanied by the anodic oxidation of this coating. The potential regions of deposition of tin, antimony, tin-antimony alloy, and mixture of this metals and their hydroxides in the pyrophosphate-tartrate electrolyte were revealed by the cyclic voltammetric method. The possibility of oxidation of cathodic deposit consisting of tin and Sn(II) hydroxide compounds to the hydrated tin dioxide in the same electrolyte was demonstrated.The operations of alloy underlayer deposition and oxidation of multilayer metal-hydroxide coating were proposed to carry out in the diluted pyrophosphate-tartrate electrolyte, similar to the main electrolyte.The accelerated tests showed higher service life of the titanium electrode with multilayer antimony-doped tin dioxide coating compared to both electrode with single-layer electrodeposited coating and the electrode with the coating obtained using prolonged heat treatment step.
منابع مشابه
Reaction pathways and mechanisms of the electrochemical degradation of phenol on different electrodes.
Laboratory experiments were carried out on the kinetics and pathways of the electrochemical (EC) degradation of phenol at three different types of anodes, Ti/SnO2-Sb, Ti/RuO2, and Pt. Although phenol was oxidised by all of the anodes at a current density of 20 mA/cm2 or a cell voltage of 4.6 V, there was a considerable difference between the three anode types in the effectiveness and performanc...
متن کاملInsights into the mechanism of electrochemical ozone production via water splitting on the Ni and Sb doped SnO2 catalyst.
The H2O splitting mechanism is a very attractive alternative used in electrochemistry for the formation of O3. The most efficient catalysts employed for this reaction at room temperature are SnO2-based, in particular the Ni/Sb-SnO2 catalyst. In order to investigate the H2O splitting mechanism density functional theory (DFT) was performed on a Ni/Sb-SnO2 surface with oxygen vacancies. By calcula...
متن کاملElectrochemical evaluation of corrosion protection performance of epoxy/polyaniline-imidazole modified ZnO nanocomposite coating on mild steel
In this research, ZnO nanoparticles modified with imidazole in O-xylene solution and characterized with Fourier transform infrared FTIR spectroscopy. Then, polyaniline-ZnO unmodified and imidazole modified nanocomposites were synthesized via in-situ emulsion polymerization method. The synthesized nanocomposites were characterized by FTIR and scanning electron microscopy SEM. The anti-corrosion ...
متن کاملCore–shell structured hollow SnO2–polypyrrole nanocomposite anodes with enhanced cyclic performance for lithium-ion batteries
0.1016/j.nanoen.2 lsevier Ltd. All rig thors. : [email protected] Abstract Core–shell structured hollow SnO2–polypyrrole (PPy) nanocomposites (SnO2@PPy) with excellent electrochemical performance were synthesized using a hydrothermal method followed by an in situ chemical-polymerization route. The thickness of the polymerized amorphous PPy coating covering on the hollow SnO2 microspheres is abou...
متن کاملAn Electrochemical Measurement for Evaluating the Cathodic Disbondment of Buried Pipeline Coatings under Cathodic Protection
Steel pipelines are susceptible to corrosion by the action of corrosive substance in the environment and one of the most common failure modes in buried pipeline coatingis cathodic disbondment. Consequently, Electrochemical Impedance Spectroscopy (EIS) was used to assess the effect of three important parameters, the thickness of coating, the artificial defect ...
متن کامل