Kinetics of Isothermal Degradation studies by Thermogravimetric Data: Effect of orange peels ash on thermal properties of High density polyethylene (HDPE)
نویسندگان
چکیده
Abstrcat High density polyethylene (HDPE) composite reinforced with 20wt% orange peels ash particles (OPAp) was prepared by compression moulding. Thermogravimetric analysis (DTA/TGA) (space) was conducted on the HDPE/orange peels ash particle composite to clarify the effect of OPAp on the thermal decomposition behavior of the resultant composite. The values of the activation energy for thermal decomposition reflected the improvement of the thermal stability of the HDPE/OPAp composite. This study has established that the orange peels ash particles are beneficial to act as thermal decomposition resistant and reinforcing particles in the HDPE matrix composite.
منابع مشابه
Pyrolysis Kinetics of Waste High-density Polyethylene using Thermogravimetric Analysis
Thermal behavior of plastic materials can be improved by knowing thermal degradation kinetics for the optimal design and operation of pyrolysis process. In the present study, thermogravimetric analysis has been used for the non-isothermal kinetic study of waste high-density polyethylene pyrolysis under nitrogen atmosphere at different heating rates 10, 20 and 40 °C/min. The kinetic parameters, ...
متن کاملCharacterizing films of polyethylene blends: An application of colorimetric parameters measurements
This study reports an application of instrumental color measurement for quantifying and comparing the optical properties of high density polyethylene HDPE and low density polyethylene LDPE blend films and the effect of blending ratio and miscibility on these properties. The technique of spectrophotometry in transmission and reflectance modes can be used as a versatile tool to evaluate the color...
متن کاملThermal and catalytic degradation study of polyethylene and investigation the catalytic effect of X-Zeolite and Silica-Alumina on degradation kinetic
The thermal degradation of polyethylene (PE) was carried out in the absence and presence ofcatalystes X-Zeolite and Silica-Alumina at different temperatures. The optimum PE/Catalysisratio was 0.25:0.05 g/g, which produced highest degradation value. PE and PE/Catalysis werecharacterized by thermogravimetric analysis. The thermal degradation properties of polymerhave been studied by Infrared spec...
متن کاملNon-Isothermal Degradation Kinetics of High Energy Protons Irradiated Polyvinyl Butyral
This research is aimed to undertake a comparative study on stability and thermal degradation kinetics of un-irradiated and high energy protons irradiated polyvinyl butyral (PVB) based on weight loss analysis and non-isothermal approaches. The weight loss by the un-irradiated PVB upon heating was found to be in two stages but due to high energy protons accelerated exposure following by chemical ...
متن کاملDetermination of Thermal Properties and Morphology of Eucalyptus Wood Residue Filled High Density Polyethylene Composites
Thermal behaviors of eucalyptus wood residue (EWR) filled recycled high density polyethylene (HDPE) composites have been measured applying the thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). Morphology of the materials was also studied using scanning electron microscope (SEM). Addition of the EWR into the recycled HDPE matrix reduced the starting of degradation tem...
متن کامل