Prediction of fatigue life of high-heat-load components made of oxygen-free copper by comparing with Glidcop
نویسندگان
چکیده
Following a successful study on the prediction of fatigue life of high-heat-load components made of Glidcop, the thermal limitation of oxygen-free copper (OFC), which is used more commonly than Glidcop, has been studied. In addition to its general mechanical properties, the low-cycle-fatigue (LCF) and creep properties of OFC were investigated in detail and compared with those of Glidcop. The breaking mode of OFC, which was observed to be completely different from that of Glidcop in a fatigue fracture experiment, clarified the importance of considering the creep-fatigue interaction. An additional LCF test with compressive strain holding was conducted so that the creep-fatigue life diagram for out-of-phase thermal fatigue could be obtained on the basis of the strain-range partitioning method. The life predicted from elasto-plastic creep analysis agreed well with that determined from the void ratio estimated in the fatigue fracture experiment.
منابع مشابه
Fatigue life prediction for high-heat-load components made of GlidCop by elastic-plastic analysis.
A procedure to predict the fatigue fracture life of high-heat-load components made of GlidCop has been successfully established. This method is based upon the Manson-Coffin equation with a cumulative linear damage law. This prediction was achieved by consolidating the results of experiments and analyses, and considered the effects of environment and creep. A low-cycle-fatigue test for GlidCop w...
متن کاملThermal Fatigue Life Prediction of Glidcop® Al-15
Photon absorbers, masks, and shutters of the third-generation light sources are subjected to intense thermal stress cycles from the high intensity x-ray beams. A collaborative research study is underway at APS and ESRF to establish thermal fatigue design criteria for Glidcop® Al-15, which is commonly used for high-heat-load components. A nonlinear finite element methodology is used for modeling...
متن کاملFatigue Life of Graphite Powder Mixing Electrical Discharge Machining AISI D2 Tool Steel
The present paper deals with the design of experimental work matrices for two groups of experiments by using Response surface methodology (RSM). The first EDM group was dealt with the use of kerosene dielectric alone, while the second was treated by adding the graphite micro powders mixing to dielectric fluid (PMEDM). The total heat flux generated and fatigue lives after EDM and PMEDM models we...
متن کاملFatigue Life Prediction of Rivet Joints
Strength reduction in structures like an aircraft could be resulted as cyclic loads over a period of time and is an important factor for structural life prediction. Service loads are emphasized at the regions of stress concentration, mostly at the connection of components. The initial flaw prompting the service life was expected by using the Equivalent Initial Flaw Size (EIFS) which has been re...
متن کاملPrediction of Fatigue Life in Notched Specimens Using Multiaxial Fatigue Criteria
In this research, the effects of notch shape on the fatigue strength of 2024-T3 aluminum alloy notched specimens have been studied using experimental and multiaxial fatigue analysis. For this purpose, four set of specimens with different notch shape were prepared and then fatigue tests were carried out at various cyclic longitudinal load levels. Load controlled fatigue tests of mentioned specim...
متن کامل