Highly reversible capacity at the surface of a lithium-rich manganese oxide: a model study using an epitaxial film system.
نویسندگان
چکیده
Epitaxial films of Li2MnO3 were synthesized using pulsed laser deposition. A 12.6 nm film exhibited a high discharge capacity of over 300 mA h g(-1) following its fiftieth cycle and better stability than 29.8 and 47.8 nm films. The surfaces of such films are intrinsically active at the electrochemical interface.
منابع مشابه
Initial Discharge Capacity of Manganese Cobaltite as Anode Material for Lithium Ion Batteries
Nanostructured manganese cobalt oxide spinel (MnCo2O4) are prepared by co-precipitation method and calcined at 650 and 750°C. Morphological studies show that by increasing the calcination temperature from 650 to 750°C, morphology of the particles changes from quasi-plate to polyhedral. The MnCo2O4 calcined at 650°C could deliver an initial discharge capacity of 1438 mAh g-1 under current densit...
متن کاملPhotocatalytic degradation of an azo textile dye with manganese-doped ZnO nanoparticles coated on glass
Mn doped ZnO nanocomposite thin film coated on glass by a simple spin-coating method was used to degrade an azo textile dye from aqueous environment. Mn doped ZnO nanocomposite thin film was characterized by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM). The photo-reduction activity of photocatalyst was evaluated using an azo textile dye as organic contaminant irradiat...
متن کاملPhotocatalytic degradation of an azo textile dye with manganese-doped ZnO nanoparticles coated on glass
Mn doped ZnO nanocomposite thin film coated on glass by a simple spin-coating method was used to degrade an azo textile dye from aqueous environment. Mn doped ZnO nanocomposite thin film was characterized by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM). The photo-reduction activity of photocatalyst was evaluated using an azo textile dye as organic contaminant irradiat...
متن کاملAdsorption Mechanism of Lead on Wood/Nano-Manganese Oxide Composite
Discharge of untreated industrial wastewater containing heavy metals such as Pb2+ is hazardous to the environment due to their high toxicity. This study reports on the adsorption, desorption, and kinetic study on Pb2+ removal from aqueous solutions using wood/Nano-manganese oxide composite (WB-NMO). The optimum pH, contact time and temperature for adsorption were found...
متن کاملNanostructured LiMn2O4 prepared by a glycine-nitrate process for lithium-ion batteries
Porous nanostructured spinel LiMn2O4 has been successfully synthesized using a glycine-nitrate combustion process. The average primary particle size of the as-synthesized powders was about 10 nm, but increased to about 100 nm with improved crystallinity after calcination at 800 jC for 2 h. Yet, the calcined powders were still highly porous and displayed reversible capacity of about 112 mA h g 1...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 51 9 شماره
صفحات -
تاریخ انتشار 2015