Enhancement of corrosion protection of AISI 304 stainless steel by nanostructured sol–gel TiO2 films
نویسندگان
چکیده
0010-938X/$ see front matter 2013 Elsevier Ltd. All rights reserved. http://dx.doi.org/10.1016/j.corsci.2013.07.045 ⇑ Corresponding author. Address: Faculty of Mechanical Engineering and Naval Architecture, Departmet of Materials, Ivana Lučića 5, 10000 Zagreb, Croatia. Tel.: +385 1 616 8313; fax: +385 1 615 7126. E-mail address: [email protected] (L. Ćurković). Lidija Ćurković a,⇑, Helena Otmačić Ćurković , Sara Salopek , Marijana Majić Renjo , Suzana Šegota d
منابع مشابه
Design and investigation of TiO2 –SiO2 thin films on AISI 316L stainless steel for tribological properties and corrosion protection
The TiO2–SiO2 thin films were deposited on AISI 316L stainless steel via sol-gel method. Then, the effect of the added amount of SiO2 on the structure, morphology and mechanical properties of the films and corrosion behavior of AISI 316L stainless steel substrate were investigated. So, X-ray diffraction, field-emission scanning electron microscopy, atomic force microscopy, depth-sensing indenta...
متن کاملGenotoxicity Effects of Ceramic Coatings Applied on Metallic Substrates using Single Cell Gel Electrophoresis Assay In Vitro
Sol-Gel coatings are a good choice for protection and bioactivation of metals used as dentistry and standard surgical implant materials. These films should both prevent degradation of the substrates by wear or corrosion, and bioactivate the material for inducing the formation of a hydroxyapatite (HA) rich layer onto the material surface, thereby permitting a natural bonding to living tissues. T...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملELECTROCHEMICAL BEHAVIOUR OF AISI 304 STAINLESS STEEL IN SULFURIC SOLUTION: EFFECTS OF ACID CONCENTRATION
The effects of H2SO4 concentration on the electrochemical behaviour of passive films formed on AISI 304 stainless steel were investigated using by potentiodynamic polarization, Mott–Schottky analysis and electrochemical impedance spectroscopy (EIS). Potentiodynamic polarization indicated that the corrosion potentials were found to shift towards negative direction with an increase in solution co...
متن کامل