Electrical and optical characterization of Ag2V4O11 and Ag4V2O6F2
نویسندگان
چکیده
The two silver vanadium oxide phases— Ag2V4O11 and Ag4V2O6F2—were prepared by hydrothermal synthesis. The electrical conductivity of both silver vanadate powders was determined by the powder-solutioncomposite (PSC) method. The conductivities obtained were 0.0085±0.0005 and 0.0005±0.00015 S/cm for the Ag2V4O11 and Ag4V2O6F2, respectively, the first such report for the Ag4V2O6F2 phase. The optical gap and the transmission where studied by diffuse reflectance. Both were larger for Ag4V2O6F2 than Ag2V4O11, concomitant with a decrease in carrier content.
منابع مشابه
Room Temperature Synthesis of the Larger Power, High Silver Density Cathode Material Ag4V2O6F2 for Implantable Cardioverter Defibrillators
New cathode materials will lead to technological advances for implantable cardioverter defibrillators, ICDs, such as reduced size and increased performance of the device. While the industry standard silver vanadium oxide Ag2V4O11 exhibits great chemical/electrochemical stability, dense silver oxide fluoride materials are advantageous because of high crystal density that can result in an increas...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملAn Overview and Feasibility Study of Fabrication Technology and Characterization Techniques of Erbium-Doped Fiber amplifiers in Iran
In this paper, a brief summary of different methods of fabrication of optical preform and fiber is reviewed. Several methods of incorporation of erbium ions into optical preforms are studied. Characterization of the fabricated erbium doped fibers including measurements of refractive index profile, absorption, fluorescence and gain spectra and metastable lifetime are described. It is also expres...
متن کاملSynthsis of Ag2O2 Semiconductor Micropowder by Plasma Electrolysis Methode and its Optical Characterization
Plasma electrolysis is a novel method for synthesis and processing of materials and nanomaterials, which uses plasma-solution interaction. In this paper, a simple setup of pin-to-solution electrical discharge with aqueous solution of silver nitrate in normal air is used. Experimental observations show that by start of electrical discharge and formation of air plasma between metal pin and soluti...
متن کامل