Corrosion and corrosive wear of annealed, impact-fractured and slow bending-fractured surface layers of AISI 1045 steel in a 3.5% NaCl solution
نویسندگان
چکیده
Previous studies have demonstrated that the wear-corrosion synergism can be markedly affected by the loading speed. In this study, effects of the loading speed or strain rate on corrosion and corrosive wear of annealed, impact-fractured and slow bending-fractured surface layers of AISI 1045 steel in a 3.5% NaCl solution were investigated using electrochemical, scanning Kelvin probing and electrochemical s f m m ©
منابع مشابه
A Comparative Study of Corrosive-Erosive Effects at AISI D3 Steel, 304 Stainless Steel and CrN/AlN Material
Corrosive-erosive effect on AISI D3 steel, 304 stainless steel and CrN/AlN coating in aqueous NaCl slurries was studied. CrN/AlN multilayer films with a thickness of 3 m and bilayer period of = 60 nm (50 bilayers) were obtained by using the physical vapor deposition (PVD) technique (magnetron sputtering). The corrosion-erosion experiments were performed in a test machine in which the impingemen...
متن کاملDuplex Surface Treatment of AISI 1045 Steel via Plasma Nitriding of Titanized Layer
In this Study, surface of medium carbon steel (AISI 1045) was modified by titanizing followed by plasma nitriding. Titanizing was performed using pack cementation method, in a pack mixture of ferrotitanium, ammonium chloride and alumina, at 1223 K for 45 and 180 min. Plasma-nitriding was conducted at two temperatures of 803 and 823 K for 5 h, in a gas mixture of 75%N2+25%H2. The samples were c...
متن کاملCorrosion Fatigue of 17-4pH Stainless Steel in a Simulated Sea Water Solution
Since martensitic precipitation hardened 17-4pH stainless steel has been widely used in corrosive environments, evaluation of its corrosion fatigue behavior is important. In this research, after microstructural studies, mechanical, corrosion, fatigue and corrosion fatigue tests were performed on 17-4pH specimens. Fatigue and corrosion fatigue tests were carried out at the stress ratio of -1 an...
متن کاملCorrosion Behaviour of Nickel Coated AISI 316 Stainless Steel as a Function of Annealing Temperature
AISI 316 stainless steels were coated with 250 nm Ni film by electron beam deposition and post-annealed at different temperatures with a nitrogen flow of 600 cm3min-1 nitrogen. The prepared samples were corrosion tested in 1.0 M sulphuric acid solution using potentiodynamic technique. Crystallographic and morphological structure of the samples were analyzedanalysed by X-ray diffraction (XRD) an...
متن کاملThe effect of TiO2 concentration on microstructure, corrosion behavior and wear behavior of Ni-P-W-TiO2 coating
Nickel-phosphorus coatings (Ni-P) are widely used in industry due to their high hardness, corrosion resistance and very good mechanical and chemical properties. Oxide particles such as TiO2 can be used to increase the wear resistance of these coatings. In this study, the Ni-P-W-TiO2 composite coating was deposited on the AISI 304L steel substrate using the electroplating method. Electroplating ...
متن کامل